The effects of Ce addition on the microstructure, age hardening response and mechanical properties of an indirect-extruded Mg-5wt.%Sn-4Zn (TZ54) alloy were investigated. Addition of Ce accelerated the aging response with the peak aging time moving from 300 h in TZ54 to 30 h in Mg-5wt.%Sn-4Zn-1Ce (TZE541), while the peak harness was similar to each other. The addition of Ce also caused an increase in the precipitation stability during overageing. Though the tensile strength of extruded TZ54 was improved by t...
The effects of Ce addition on the microstructure, age hardening response and mechanical properties of an indirect-extruded Mg-5wt.%Sn-4Zn (TZ54) alloy were investigated. Addition of Ce accelerated the aging response with the peak aging time moving from 300 h in TZ54 to 30 h in Mg-5wt.%Sn-4Zn-1Ce (TZE541), while the peak harness was similar to each other. The addition of Ce also caused an increase in the precipitation stability during overageing. Though the tensile strength of extruded TZ54 was improved by t...
基金
Project supported by the Fundamental R&D Program for Core Technology of Materials Funded by the Ministry of Knowledge Economy and the Center for Advanced Materials Processing (CAMP) of 21st Century Frontier R&D Program, Republic of Korea