钛酸钾晶须界面性质研究 被引量:16

The Interface Properties of Potassium Titanate Whiskers
下载PDF
导出
摘要 通过乳液聚合的方法对钛酸钾晶须进行表面改性,获得了表面包裹聚甲基丙烯酸甲酯的钛酸钾晶须.FT-IR、SEM、EDS的表征表明,钛酸钾晶须的表面包裹了聚甲基丙烯酸甲酯膜,形成了以钛酸钾晶须为核,聚甲基丙烯酸甲酯为壳的复合粒子.研究表明,改性后的晶须表面能降低,在有机溶液中的界面张力大大降低,与聚甲基丙烯酸甲酯的界面性质相似,说明改性后的晶须基本被聚甲基丙烯酸甲酯完全包裹,因此晶须由亲水性变为疏水性,在有机溶液中的分散性显著提高. This paper investigated a method of modifying potassium titanate whiskers (K2O . 6TiO(2)) to obtain polymethyl methacrylate (PMMA) / K2O . 6TiO(2) Composite particles through emulsion polymerization. The interface properties of pure and modified potassium titanate whiskers were studied in details. According to the characterizations of FT-IR, SEM and EDS, the surface of the potassium titanate whiskers was covered by PMMA molecules and the composite particles have a core-shell structure. The characterization of surface energy and interfacial tension showed that the interface property of modified whiskers has changed thoroughly and it was similar to that of PMMA, so the whiskers were covered by PMMA thoroughly. It made the potassium titanate whiskers modified from hydrophilic to hydrophobic and the dispersibility of the whiskers in organic liquids improved greatly.
出处 《物理化学学报》 SCIE CAS CSCD 北大核心 2004年第8期868-870,共3页 Acta Physico-Chimica Sinica
基金 国家杰出青年科学基金(29925616) 国家自然科学重点基金(20236010) 国家自然科学基金(20246002) 国家高技术研究发展规划(863项目)(2003AA333010)资助~~
关键词 钛酸钾晶须 表面改性 分散 表面能 界面张力 乳液聚合 potassium titanate whiskers surface modification dispersion surface energy interfacial tension emulsion polymerization
  • 引文网络
  • 相关文献

参考文献14

  • 1Ou,Y.C.;Yang,F.Chen,J.J.Appl.Polym.Sci.,1997,64(12): 2317
  • 2Tjong,S.C.;Meng,Y.Z.J.Appl.Polym.Sci.,1999,72(4):501
  • 3Feng,X.Ph.D.Dissertation.Nanjing:Nanjing University of Technology,2000 [冯新 .博士学位论文 .南京 :南京工业大学 ,2000]
  • 4Hasegawa,M.;Kanda,Y.Powder Technol.,1994,78(2):159
  • 5Iketani,K.;Sun,R.D.;Toki,M.;Hirota,K.;Yamaguchi,O. J.Phys.Chem.Solids,2003,64(3):507
  • 6Zhang,Y.;Wang,M.Q.J.Non-Cryst.Solids,2000,271(1-2): 88
  • 7Luna-Xavier,J.L.;Guyot,A.;Bourgeat-Lami,E.J.Colloid. Interf.Sci.,2002,250(1):82
  • 8Xie,J.W.;Lu,X.H.;Zhu,Y.;Liu,C.;Bao,N.Z.;Feng,X. J.Mater.Sci.,2003,38:3641
  • 9Tamai,Y.;Makuuchi,K.;Suzuki,M.J.Phys.Chem.,1967,71 (13):4176
  • 10Fowkes,F.M.Ind.Eng.Chem.,1964,56(12):40

二级参考文献26

共引文献83

同被引文献139

引证文献16

二级引证文献85

;
使用帮助 返回顶部