聚苯硫醚及其玻璃纤维增强复合材料力学性能研究 被引量:3

STUDY ON THE MECHANICAL PROPERTIES OF CONTINUOUS GLASS FIBER REINFORCED POLY(PHENYLENE SULFIDE) COMPOSITES
下载PDF
导出
摘要 本文利用差示扫描量热仪(DSC)研究了国产低分子量聚苯硫醚及其固相热处理产物的热行为,并用悬浮-熔融法制备了玻璃纤维增强聚苯硫醚复合材料的预浸带,测定了其单向板的力学性能,观察了其断口形貌。结果表明:低分子量聚苯硫醚经过固相热处理后,其T_g、T_c上升,T_m下降;热处理后的聚苯硫醚玻纤复合材料在室温时的力学性能有很大程度的提高,其高温性能受玻璃化转变的影响显著;通过SEM观察断口发现其破坏主要属于界面脱粘。 The domestic Poly (phenylene sulfide) (PPS) was cured in air at 270°C, and the melting behavior of PPS and CL-PPS (cured) as well as the processing and mechanical properties of their composites reinforced with glass fiber were studied in this paper. The results show that Tg and Tc of the resin increase after it is cured, but its Tm become lower. The prepreg of glass fiber reinforced PPS was manufactured by suspension-mel-ting method. The mechanical properties of GF/CL-PPS composite such as impact strength, shear strength, flexural strength and flexural modulus are improved more than those of GF/PPS at room temperature, and they have very good chemical resistance. The mechanical properties of both GF/PPS and GF/CL-PPS change greatly within their glass transition temperature regions. SEM indicates that the fracture mainly occurs in the interface between glass fibers and PPS resin.
出处 《复合材料学报》 EI CAS CSCD 北大核心 1993年第3期29-35,共7页 Acta Materiae Compositae Sinica
基金 航空航天部七.五预研课题
关键词 聚苯硫醚 热处理 复合材料 poly(phenylene sulfide), teat treatment, suspension-melting method, GF/PPS composite
  • 引文网络
  • 相关文献

参考文献3

共引文献2

同被引文献27

引证文献3

二级引证文献18

;
使用帮助 返回顶部