摘要
论述了锆包壳产生碘致应力腐蚀的原因,综述了碘致应力腐蚀的开裂机理和碘致应力腐蚀的影响因素,指出碘致应力腐蚀的影响因素包括:温度、微结构、碘分压和化学因素。
The cause of iodine-induced stress corrosion crack of zirconium cladding is described in this paper. Mechanism and effect factors of iodine-induced stress corrosion crack are discussed. It points out that the effect factors of iodine-induced stress corrosion crack include temperature, microstructure, iodine fractional pressure and chemical factor.