高锆Si-Al-Zr-O系非晶晶化过程 被引量:3

Crystallization behavior of Si-Al-Zr-O amorphous bulk with higher zirconium
下载PDF
导出
摘要 采用差示扫描量热分析(DSC)、X射线衍射(XRD)分析、红外光谱(IR)分析和扫描电镜(SEM)观察等方法,对Si-Al-Zr-O系非晶晶化过程、晶核剂对晶化过程的影响进行了研究.结果表明:Si-Al-Zr-O系非晶在935~970℃和1 100~1 200℃分别发生了四方氧化锆和莫来石的析出反应;TiO2和ZrO2作为晶核剂引入对四方氧化锆和莫来石的析出有一定影响;TiO2含量的增加可使四方氧化锆晶相的析出能力显著提高,而ZrO2含量的增加可提高莫来石晶相的析出能力.根据晶化过程的研究结果制定了合理的晶化热处理工艺,并获得晶粒大小均匀、结构致密的微米晶、纳米晶、莫来石/SiO2-t-ZrO2复相陶瓷. The crystallization processes of the Si-Al-Zr-O(SAZ) amorphous bulk were investigated with the aid of DSC, IR, XRD and SEM analysis. The results show that there are two crystallization reactions during the heat treatment for SAZ amorphous bulk. The first crystallization reaction occurs in the range of 935 - 970℃. The tetra- gonal zirconia is formed. The second crystallization reaction occurs in 1 100 - 1 200 ℃. The main phases precipitated are mullite and cristobalite. The additions of ZrO2 , TiO2 are useful to improve the crystallization behavior. With TiO2, ZrO2 content increase, crystallization temperature decreases. According to the investigation results, a nanometer dense(mullite, cristobalite )/zirconia composite ceramics with uniformly dispersed zirconia not greater than 1μm are obtained after heat-treatment of the homogenous Si-Al-Zr-O amorphous bulk.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2005年第8期1189-1193,共5页 The Chinese Journal of Nonferrous Metals
基金 国家高技术研究发展计划资助项目(2003AA332040)
关键词 Si-Al-Zr-O系非晶 晶化行为 陶瓷复合材料 Si-Al-Zr-O system crystallization behavior ceramic composite
  • 引文网络
  • 相关文献

参考文献18

  • 1肖汉宁,彭文琴,邓春明.微晶陶瓷的制备技术、性能及用途[J].中国陶瓷,2000,36(5):31-33. 被引量:40
  • 2LIANG Shu-quan, TANG Xiao-ping, TANG Yan.Research on Si-Al-Zr-O composite ceramics with ultra fine grains [A]. Proceedings of International Workshop on Research Science and Engineering of Rare Metals[C]. Akita, Japan:Akita University Press,2004. 305-313.
  • 3谭业发,王耀华,于爱兵,徐燕申,唐文彪,刘维民.氧化锆增韧莫来石复相陶瓷的摩擦磨损行为与磨损机制[J].摩擦学学报,2000,20(2):94-97. 被引量:10
  • 4Lathabai S, Hay D G, Wagner F, et al. Reactionbonded mullite/zirconia composites[J]. J Am Ceram Soc, 1996, 79(1):248-256.
  • 5Moya J S, Osendi M I. Effect of ZrO2 in mullite on the sintering and mechanical properties of mullite/ZrO2 composites[J]. J Mater Sci Lett, 1983, 2:599- 601.
  • 6Orange G, Fantozzi G, Cambier F, et al. High temperature mechanical properties of reaction-sintered mullite/zirconia and mullite/aluminia/zirconia composites[J]. J Mater Sci, 1985, 20:2533-2540.
  • 7YUAN Qi-ming, JAN Jia-qi, JIN Zheng-guo. Preparation and properties of zirconia-toughened mullite ceramics[J]. J Am Ceram Soc, 1986, 69(3):265-270.
  • 8Khor K A, Yu L G, Li Y, et al. Spark plasma reaction sintering of ZrO2-mullite composites from plasma spheroidized zircon/alumina powers[J]. Mater Sci Eng A, 2003, A339:286-296.
  • 9Giess E A, Roldan J M, Bailey P J, et al. Microstructure and dielectric properties of mullite ceramics[A].Nair K M, Pohanka R C, Buchanan R C. Ceramic Transactions, Microelectronics Systems(vol. 15)[C].Westerville, OH:American Ceramic Society, 1990.167-172.
  • 10Chu J I, Park H C, Sorrell C C. DTA study of nucleation and crystallization of MgO-CaO-SiO2-P23 O5 glass-ceramics containing ZrO2, BaCO3 and Li2CO3[J]. IntCeramMonogr, 1994, 1:585-590.

二级参考文献12

共引文献48

同被引文献6

引证文献3

二级引证文献6

;
使用帮助 返回顶部