金属注射成形17-4PH不锈钢的研究 被引量:7

Metal injection molding 17-4PH stainless steel
下载PDF
导出
摘要 研究了17-4PH不锈钢的金属注射成形工艺及其流变学性能、力学性能、微观组织和耐腐蚀性能。结果表明:采用65%PW-30%EVA-5%SA粘结剂组成的注射料具有最好的综合流变学性能。在1 380℃保温90 min的烧结条件下,注射成形17-4PH不锈钢的力学性能最佳,孔隙分布均匀,晶粒尺寸适中。而保温60和120 min则分别表现出烧结不完全和过烧现象。1 380℃保温90 min烧结所得到的力学性能为ρ=7.70 g/cm3,σb=1 275 MPa,δ=5%,硬度36 HRC。注射成形17-4 PH不锈钢的密度、抗拉强度、硬度随着烧结温度的升高而提高,伸长率则随着烧结温度的升高而下降。17-4 PH不锈钢的耐蚀性好,腐蚀期长,具有活化-化金属极化曲线的特征,但钝化电位范围较窄,耐点蚀性能较差。 The rheological properties, mechanical properties, microstructure and anticorrosive properties of injection molded 17-4 PH stainless steel were investigated. The feedstock based on the binder 65% PW-30%EVA-5% SA has the best general rheological properties for the 17-4 PH stainless steel powder. The 17-4 PH stainless steel compacts sintered at 1380℃ for 90min have the best mechanical properties and the good microstructure with homogeneously distributed pore structure and the moderate-sized grains. Whereas the compacts sintered for 60min and 120min show the inadequate sintered microstructure and the over-sintered microstructure respectively. The compacts sintered at 1380℃ for 90min have the density of 7.70g/cm^3, the strength of 1275MPa, the elongation of 5%, and the hardness of 36 HRC. With the increase of sintering temperature, the density, strength and the hardness increase, whereas the elongation decreases. The 17-4 PH stainless steel has good anticorrosive properties and the long corrosion period. It has an activation-passivation polarization curve, but the passivation potential range is narrow. The spot corrosion is relatively easy to occur.
出处 《粉末冶金技术》 EI CAS CSCD 北大核心 2005年第4期254-258,共5页 Powder Metallurgy Technology
基金 国家"八六三"计划资助项目(2001AA337050) 霍英东基金资助项目(81041) 全国优秀博士学位论文作者专项基金资助项目(200135)
  • 引文网络
  • 相关文献

参考文献13

  • 1German R M., Hens K F. Key issues in powder injection molding.Ceramic Bulletin, 1991, 70(8) : 1294 -- 1302.
  • 2German R M.. Technological barriers and opportunities in powder injection molding. Powder Metall Int, 1993,25(4) : 165-- 169.
  • 3Kulkarni K M.. Future looking bright for PIM. Metal Powder Report, 55(10), 2000:40--42.
  • 4Clifford B, Michael Z. Advances in powder injection molding. Annual Technical Conference-ANTEC, New York, 1998. Conference Proceedings, v 1,358--361.
  • 5Hauek P A. Powder injection molding: Current and long term outlook. International Journal of Powder Metallurgy, 2000,36(3) : 29--30.
  • 6German R M . Scientific status of metal powder injection molding.International Journal of Powder Metallurgy, 36 (3), 2000 : 31 -- 36.
  • 7PIM97: 1st European Sym. on PIM, Powder Metallurgy, 1997,40(4) : 262.
  • 8Shah J, Nunn R E. Rheology of metal injection molding feedstock.Powder Metall. Int, 1987, 19(6): 38.
  • 9Li Yimin, Qu Xuanhui, Huang Baiyun, et al. Rheologieal properties of metal injection molding binder and feedstock. Tran Nonferrous Met Soc China, 1999,7(3):103.
  • 10Novae O A, Anton D, Novae T. The rheological behavior of some binders and plastisols used in injection molding. PM'94 Conference, Paris, 1994.

同被引文献91

引证文献7

二级引证文献15

;
使用帮助 返回顶部