新型含镁铝尖晶石的铝酸盐水泥的研究(英文) 被引量:1

A study on new type aluminous cements containing magnesium aluminate spinel
下载PDF
导出
摘要 以白云石和工业三氧化二铝为原料,采用反应烧结技术制得了含镁铝尖晶石的铝酸盐水泥,探讨了原料及烧结温度和添加剂对含镁铝尖晶石的铝酸盐水泥性能的影响,XRD结果表明产物的物相组成为MA,CA,CA2;采用扫描电镜(SEM)及能谱(EDS)对产物的显微结构进行了观察与分析。结果表明:以轻烧白云石和工业Al2O3为原料制得的水泥具有较高的结合强度;所制得的含镁铝尖晶石的铝酸盐水泥的显微结构较为均匀,外加剂CaCl2具有明显的早强效果。 A new type of calcium aluminate cement containing MA spinel was produced by sintering the raw materials of dolomite and alumina mixture. The effects of raw materials and sintering temperature and additives on the properties of cements was were investigated. X-ray diffraction (XRD) results indicate that the final products consisted of CA, CA2 and MA. The microstructure of product was analyzed by means of scanning electron microscope (SEM) and energy dispersive spectrometry (EDS). The experiments results showed that the cement had the satisfied cold bonding strength and sintering properties when the light-burned dolomite and alumina were employed and fired at 1600℃. The new type cements has relatively uniform microstructure The early stage strength of the refractory castables bodies was greatly improved by adding 2wt.% of CaCl2 as a strength modifier.
出处 《西安建筑科技大学学报(自然科学版)》 CSCD 北大核心 2005年第3期411-415,共5页 Journal of Xi'an University of Architecture & Technology(Natural Science Edition)
基金 陕西省教育厅专项基金项目(2004JK216) 陕西省自然科学基金项目(2004E107)~~
  • 引文网络
  • 相关文献

参考文献7

  • 1Korgul P,Wilson D R,Lee W E. Microstructural analysis of corroded alumina-spinel castable refractories[J]. J.Eur. Ceram. Soc., 1997,(17):77-84.
  • 2Aza A H, Iglesias J E, Pean P, et al. The system Al2O3-MgO CaO. Part I: phase relationship in the subsystem Al2O3- MgAl2O4- CaAl4O7[J]. J. Am. Ceram. Soc,1999,82(8) :2193-2203.
  • 3Aza A H, Iglesias J E, Pen P,et al. The system Al2O3-MgO CaO. Part Ⅱ :phase relationship in the subsystem Al2O3- MgAl2O4- CaAl4O7[J]. J. Am. Ceram. Soc. ,2000,84 (4): 919-927.
  • 4De Aza AH, Pena P, Rodriguez MA,et al. New spinel-containing refractory cements [J]. J. Eur. Ceram.Society, 2003, (23): 737-744.
  • 5Khalil Nagy MA,EI-Henaly SAS,Girgis Lamey G. Aluminous cements containing magnesium aluminate spinel from Egyptian dolomite[J]. Ceramics International, 2001, (27): 865-873.
  • 6Park K M,Sharp J H. Refractory calcium aluminate cements[J]. Trans. Br. Ceram. Soc. 1982, 81(2):35-42.
  • 7LU Pei-wen. Silicate Physical chemistry [M]. Nanjing: Southeast University Press, 1991.

同被引文献3

  • 1张冠伦.混凝土外加剂-原理及其应用[M].上海:上海科学文献出版社,1992:88-90.
  • 2王维邦.耐火材料工艺学[M].北京:冶金工业出版社,1981:67-69.
  • 3黄大能.新拌混凝土的结构与流变特征[M].北京:中国建筑工业出版社:1981.134-136.

引证文献1

二级引证文献2

;
使用帮助 返回顶部