The ratio of Fe-Al compound at interace, which could determine the quarttity of Fe-Al compound at the interace of steel-mushy Al- 20 Sn bonding plate, was used to characterize the interfacial structure of steel-mushy Al-20 Sn bonding plate quantitatively. The effect of ratio of Fe-Al compound at interface on interacial shear strength was investigated perfectly. The results show that the relationship between ratio of Fe-Al compound at interace and interfacial shear strength is S = 3.3 ＋ 1.91 t - 0.0135t^2 （ where t is ratio of Fe-Al compound at in- terface and S is interfacial shear strength ）. When the ratio of Fe-Al compound at interface is 71%, the largest interfacial shear strength 70.9 MPa is got. This reasonable ratio of Fe-Al compound at interface is a quarttitative criterion of interfacial embrittlement. When the ratio of Fe-Al compound at interface is higher than 71% , interfacial embrittlement will occur.
The ratio of Fe-Al compound at interace, which could determine the quarttity of Fe-Al compound at the interace of steel-mushy Al- 20 Sn bonding plate, was used to characterize the interfacial structure of steel-mushy Al-20 Sn bonding plate quantitatively. The effect of ratio of Fe-Al compound at interface on interacial shear strength was investigated perfectly. The results show that the relationship between ratio of Fe-Al compound at interace and interfacial shear strength is S = 3.3 ＋ 1.91 t - 0.0135t^2 （ where t is ratio of Fe-Al compound at in- terface and S is interfacial shear strength ）. When the ratio of Fe-Al compound at interface is 71%, the largest interfacial shear strength 70.9 MPa is got. This reasonable ratio of Fe-Al compound at interface is a quarttitative criterion of interfacial embrittlement. When the ratio of Fe-Al compound at interface is higher than 71% , interfacial embrittlement will occur.
基金
Funded by the National Natural Science Foundation of China(No.50274047 and 50304001) ,BeijingJiaotong University Founda-tion and the Foundation of the Ministry of Education of China ,andthe National Science Foundation of Beijing