微量稀土Er对Al-5Mg合金组织与性能的影响 被引量:41

Effects of trace rare-earth element Er on microstructure and properties of Al-5Mg alloy
下载PDF
导出
摘要 采用铸锭冶金法,制备含不同量稀土元素Er的Al-5Mg合金。利用拉伸力学性能测试、OM、XRD、SEM、TEM及EDS分析等分析测试手段,研究微量Er对Al-5Mg合金微观组织与力学性能的影响。结果表明:Er可以明显提高Al-5Mg合金的强度,添加0.4%Er(质量分数)的Al-5Mg合金的冷轧态屈服强度(σ0.2)提高了81MPa,而延伸率变化不大;Er的加入还能减少Al-5Mg合金的枝晶偏析,并可显著细化合金的晶粒组织;Er对晶粒的细化机理与其添加量有关,当Er含量较低时,符合传统的稀土细化机理;当Er含量较高时,由于在熔体中形成了初生Al3Er质点,在结晶形核时可以作为非均质形核核心,从而可显著细化晶粒组织;Er对合金的强化效应主要来自于晶粒细化及在晶内形成的细小二次Al3Er质点。根据实验结果可知,添加0.4%Er可使合金具有较为优异的综合性能。 Al-5Mg alloys containing different content of Er were prepared hy cast metallurgy. The effect of trace Er on the microstructure and properties of Al-5Mg alloy was studied with tensile properties measurement, OM, XRD, SEM, TEM and EDS. The results show that the addition of Er to Al-5Mg alloy can improve the strength remarkably, and the yield strength of the cold-rolled alloy is improved by 81 MPa when the content of Er is 0.4% (mass fraction), while the ductility keeps stable or decreases slightly. The addition of Er can reduce the dendritical arm space of the alloy, and the grains are refined obviously. The refinement mechanism of Er addition on the grain depends on the quantity of Er added. The refinement mechanism of the alloy containing less Er conforms to be traditional refining theory on rare-earth aluminum alloy. The grain of the alloy containing more Er is refined due to the formation of primary Al3 Er, and the primary Al3Er shall he able to act as nucleus. The strengthing effect of Er on Al-5Mg alloy is caused by grain refinement and the fine secondary Al3 Er particles. The results indicate that the alloys with 0.4 % Er have more excellent properties.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2006年第5期768-774,共7页 The Chinese Journal of Nonferrous Metals
基金 国家重点基础研究发展规划资助项目(G1999064907)
关键词 ER Al-5Mg合金 AL3ER 微观组织 力学性能 Er Al-5Mg alloy Al3Er microstructure mechanical properties
  • 引文网络
  • 相关文献

参考文献16

  • 1Sawtell R R,Jensen C L.Mechanical properties and microstructures of Al-Mg-Sc alloys[J].Met Trans,1990,A21:421-430.
  • 2Filatov Y A,Yelagin V I,Zakharov V V.New Al-Mg-Sc alloys[J].Mater Sci Eng A,2000,A280:97 -101.
  • 3Kendig K L,Miracle D B.Strengthening mechanisms of an Al-Mg-Sc-Zr alloy[J].Acta Materialia,2002,(50):4165-4175.
  • 4TANG Ding-xiang,WANG Liang-xuan,ZHAO Minshou,et al.The research on rare-earth aluminum alloy in Chinese[J].The Chinese Journal of Rear-Earth,1992,10(1):66-71.
  • 5徐国富,聂祚仁,金头男,杨军军,付静波,尹志民.微量铒对LF_3铝合金铸态组织的影响[J].中国稀土学报,2002,20(2):143-145. 被引量:44
  • 6杨军军,聂祚仁,金头男,徐国富,付静波,左铁镛.微量稀土元素Er对高纯铝再结晶行为的影响[J].稀有金属材料与工程,2003,32(1):37-40. 被引量:28
  • 7NIE Zuo-ren,JIN Tou-nan,XU Guo-fu,et al.Research on rare earth in aluminum[J].Materials Science Forum,2002,396-402:1731-1735.
  • 8NIE Zuo-ren,JIN Tou-nan,ZOU Jing-xia,et al.Development on research of advanced rare-earth aluminum alloy[J].Trans Nonferrous Met Soc China,2003,13(3):509-514.
  • 9YANG Jun-jun,NIE Zuo-ren,JIN Tou-nan,et al.Effect of trace rare earth element Er on high pure Al[J].Trans Nonferrous Met Soc China,2003,13(5):1035-1039.
  • 10MondolfoLF 王祝堂 张振录 译.铝合金的组织与性能[M].北京:冶金工业出版社,1988.312,315-353.

二级参考文献4

共引文献68

同被引文献365

引证文献41

二级引证文献271

;
使用帮助 返回顶部