摘要
The precursor of ammonium aluminum carbonate hydroxide was synthesized by using aluminum sulfate（Al2（SO4）3） and ammonium carbonate（（NH4）2CO3）. The effects of α-Al2O3 seeds and mixture composed of α-Al2O3 and ammonium nitrate, as well as multiplex catalysts （AT） on phase transformation of alumina in sintering process were investigated respectively. The results show that the α-Al2O3 seeds and the mixture of α-Al2O3 and ammonium nitrate can lower the phase transformation temperature of α-Al2O3 to different extents while the particles obtained agglomerate heavily. AT has great potential synergistic effects on the phase transformation of alumina and reduces the phase transformation temperature of α-Al2O3 and the trends of necking-formation between particles. Therefore the dispersion of powder particles is improved significantly.
The precursor of ammonium aluminum carbonate hydroxide was synthesized by using aluminum sulfate （Al2 （SO4）3 ） and ammonium carbonate（（NH4 ）2CO3 ）. The effects of α-Al2 O3 seeds and mixture composed of α- Al2O3 and ammonium nitrate, as well as multiplex catalysts （AT） on phase transformation of alumina in sintering process were investigated respectively. The results show that the α-Al2 O3 seeds and the mixture of α-Al2 O3 and ammonium nitrate can lower the phase transformation temperature of α-Al2O3 to different extents while the particles obtained agglomerate heavily. AT has great potential synergistic effects on the phase transformation of alumina and reduces the phase transformation temperature of α-Al2O3 and the trends of necking-formation between particles. Therefore the dispersion of powder particles is improved significantly.