固溶处理对7A55铝合金的组织和力学性能的影响 被引量:15

Effect of solution treatment on microstructure and mechanical properties of 7A55 aluminum alloy
下载PDF
导出
摘要 通过组织观察(光学显微镜和扫描电镜)、力学性能检测、电导率测定,研究了单级固溶和双级固溶对7A55铝合金板材组织和力学性能的影响。结果表明:采用最佳单级固溶制度470℃/0.5h和120℃/24h时效处理,其力学性能σb,0σ.2和δ分别为635MPa,584MPa,和13.1%。与单级固溶处理制度相比,双级固溶处理在再结晶程度较小的情况下,能较大幅度的提高7A55铝合金板材的固溶度。采用双级固溶处理450℃/1.5h+485℃/40min,120℃/24h时效后的力学性能有较大提升,其σb,σ0.2和δ分别达648MPa,630MPa和11.2%,较单级固溶其σ0.2强度提高了7.8%。 The effects of single solution heat treatment and two-stage solution heat treatment on mierostrueture and mechanical properties of 7A55 aluminum alloy were investigated by means of optical microscopy and SEM, tensile test and electrical conductivity measurement. The optimal single solution heat treatment is 470℃/0.5h, which results in σb = 584MPa, σ0.2 = 635MPa and δ= 13.1% after aging of 120℃/24h. The two-stage solution heat treatment of 450℃/1 .Sh + 485℃/40min improves dissolution of soluble constituents in the 7A55 aluminum alloy with small degree of recrystallization, and the mechanical properties σb = 648MPa,σ0.2 = 630MPa and δ = 11.2% are obtained,and the yield strength is about 7.8% higher than that obtained by single solution heat treatment.
出处 《材料热处理学报》 EI CAS CSCD 北大核心 2007年第1期87-91,共5页 Transactions of Materials and Heat Treatment
基金 高性能铝材与铝资源的高效利用(2005CB623700)
关键词 7A55铝合金 双级固溶 力学性能 电导率 7A55 alloy two-stage solution heat treatment mechanical properties electrical conductivity
  • 引文网络
  • 相关文献

参考文献13

  • 1Deshpande N U,Gorkhale A M.Relationship between fraclure toughness,fractate path,and microstructure of 7050 aluminum alloy:Part 1.Quantitative characterization[J].Metallargical and Materials Transactions A,1998,29(4):1191-1201.
  • 2Morere B,Ehrstrom J C.Microstructural effects on fracture toughness in AA7010 plate[J].Metall and Mater A.2000,31(10):2503-2515.
  • 3Bruce Morere,Claire Maurice,Ravi Shahani,et al.The influence of Al3Zr dispersoids on the recrystallization of hol-deformed AA 7010 Alloys[J].Metall and Mater Trans A,200,32(3):625-631.
  • 4Suha Dong-Woo,Lee Surg-Yong,Lee Kyong-Hwan,et al.Microstructural evolution of Al-Zn-Mg-Cu-(Se)alloy doring hot extrusion and heat treatments[J].Journal of Materials Processing Technology,2004,155-156(30):1330-1336.
  • 5ЕЛАГИНВ В И.ВАХАРОВ[M].Обраб.Мег,1994,13(4):13.
  • 6李行旦.仿美7075高强度铝合金[J].上海金属(有色分册),1992,13(4):13-22. 被引量:5
  • 7Ronson J D.Predicting recrystallised volume fraction in aluminium alloy 7050 hot rolled plate[J].Materials Science and Technology,2002,18(6):607-614.
  • 8Robson J D.Microstructural evolution in aluminium alloy 7050 during processing[J].Materials Science and Engineering A,2004,382:112-121.
  • 9宁爱林,蒋寿生,彭北山.铝合金的力学性能及其电导率[J].轻金属,2005(6):34-36. 被引量:39
  • 10Humphreys F J,Hatherly M.Recrystallization and related annealing phenomena[M].Oxford:Elsevier Science Ltd,1995:127-173

二级参考文献12

共引文献72

同被引文献166

引证文献15

二级引证文献180

;
使用帮助 返回顶部