Mg(PO_3)_2-AlF_3-PbF_2系统玻璃振动光谱的研究

A Study of the Mg(PO_3)_2—AlF_3—PbF_2Glass Structures by Vibrational Spectroscopy
下载PDF
导出
摘要 由FT—IR和Raman光谱的结果得出:该三元系统玻璃在高磷区为偏磷酸盐结构。其结构网络主要由[O=PO_Z四面体组成的链状和少许环状分子构成。随着PbF_2含量的增加,链开始断裂。当过渡到中磷区时,又主要以[Al(O,F)_4]和[P(O,F)_4]四面体及焦磷酸盐结构状态存在。当[Al(O,F)_4]和[P(O,F)_4]两者的比值为1∶1时,将无法形成玻璃。实验结果还指出,上述系统在中磷区的形成玻璃的范围是很小的。到低磷区时,由磷氧构成的网络几乎不存在,仅以孤立的[P(O,F)_4]四面体即氟正磷酸盐结构存在,同时双键氧P=O也消失。 The results from FT—IR and Raman Spectroscopy proved that the glass structures of Mg(PO_3)_2—A1F_3—PbF_2 ternary system in the high content of phosphate are metaphosphate structures. The structure networks are basically composed of[O = PO3/2] tetrahedra chains. With increasing the content of PbF_2 the chains begin to break, and in the region of middle content of phosphate the main structures are [Al(O,F)_4] and [P(O,F)_4]tetrahedra and pyrophosphate. When the ratio of[Al(O, F)_4] and[P(O,F)_4]is equal to 1:1, the glass could not be formed.