摘要
爆炸焊接复合钢板设备在制造过程中焊接接头易产生裂纹等缺陷,对焊接接头缺陷产生原因进行分析,提出相应措施以避免缺陷产生。
Owning to some cracks will exist on the welding joint of equipments made of explosive clad plate during fabrication, so this article analysis the reasons and take some proper measures to avoid these defects.
出处
《压力容器》
北大核心
2007年第11期31-34,共4页
Pressure Vessel Technology
关键词
爆炸复合板
裂纹等缺陷
产生及防止
explosive clad plate
defects i. e. cracks
generation and prevention