细颗粒对气固流化床中静电行为的影响 被引量:8

Electrostatic behavior with fines of different sizes added into gas-solid fluidized bed
下载PDF
导出
摘要 Polymer particles having the same chemical makeup but different sizes would have their own special contributions to the generation of static charges,owing to the differences in catalyst residue and surface properties among them.Experiments were performed in a gas-solid fluidized bed to determine the changes in the electrostatic charges with addition of various fine polyethylene particles,which were the same material as the coarse polyethylene particles,to better understand their role in influencing electrostatic charge generation/dissipation.By measuring the electrostatic potential at different bed axial heights,it was found that the electric field inside the bed was significantly influenced by the size of added fine polyethylene particles,mass fractions and catalyst residue.Consequently,an impact factor of fine particles(Fb) was proposed,which was the sum of particle diameter term and catalyst residue term.Within the experimental limits in this paper,after three kinds of fines with Fb all less than 1 were added in the fluidized bed,the electrostatic potential in the bed was just influenced slightly.However,the bed electrostatic potential changed significantly following the addition of the fines with the smallest particle diameter and highest residual catalyst content.While Fb of this kind of fines was less than 1,the static potential did not change much but even decreased slightly with the addition of fines.Once Fb of the fourth kind of fines was more than 1,the electrostatic potential in the bed increased greatly.With Fb of the fourth kind of fines increasing further,the electrostatic potential fell a little,and meanwhile it was found that a large amount of fine particles adhered to the column wall. Polymer particles having the same chemical makeup but different sizes would have their own special contributions to the generation of static charges, owing to the differences in catalyst residue and surface properties among them. Experiments were performed in a gas-solid fluidized bed to determine the changes in the electrostatic charges with addition of various fine polyethylene particles, which were the same material as the coarse polyethylene particles, to better understand their role in influencing electrostatic charge generation/dissipation. By measuring the electrostatic potential at different bed axial heights, it was found that the electric field inside the bed was significantly influenced by the size of added fine polyethylene particles, mass fractions and catalyst residue. Consequently, an impact factor of fine particles (Fb) was proposed, which was the sum of particle diameter term and catalyst residue term. Within the experimental limits in this paper, after three kinds of fines with Fb all less than 1 were added in the fluidized bed, the electrostatic potential in the bed was just influenced slightly. However, the bed electrostatic potential changed significantly following the addition of the fines with the smallest particle diameter and highest residual catalyst content. While Fb of this kind of fines was less than 1, the static potential did not change much but even decreased slightly with the addition of fines. Once Fb of the fourth kind of fines was more than 1, the electrostatic potential in the bed increased greatly. With Fb of the fourth kind of fines increasing further, the electrostatic potential fell a little, and meanwhile it was found that a large amount of fine particles adhered to the column wall.
出处 《化工学报》 EI CAS CSCD 北大核心 2008年第2期341-347,共7页 CIESC Journal
基金 国家自然科学基金重大项目(20490205) 国家自然科学基金-石油化工联合基金项目(2073611)~~
关键词 气固流化床 静电荷 摩擦起电 双极带电 gas-solid fluidized bed electrostatic charge triboelectrification bipolar charging
  • 引文网络
  • 相关文献

参考文献22

  • 1Ciborawski J, Woldarski A. On electrostatic effects in fluidized beds. Chemical Engineering Science, 1962, 17:23-32
  • 2Boland D, Geldart D. Electrostatic charging in gas fluidized beds. Pozoder Technology, 1971/1972, 5:289-297
  • 3LiYanhui(李延辉).Simple analysis on the treatment eliminating static charges in LLDPE plants[J].浙江化工,32:82-86.
  • 4Gregory H. Electrostatics and gas phase fluidized bed polymerization reactor wall sheeting. Chemical Engineering Science, 2006, 61 (4): 1041- 1064
  • 5于恒修,王芳,王靖岱,阳永荣.气相聚合流化床内静电与结片现象的研究进展[J].石油化工,2007,36(2):205-209. 被引量:32
  • 6Wolny A, Opalinski I. Electric charge neutralization by addition of fines to a fluidized bed composed of coarse dielectric particles. Journal of Electrostatics, 1982, 14 (3): 279-289
  • 7Wolny A, Kazmierczak W. Triboelectrification in fluidized bed of polystyrene. Chemical Engineering Science, 1989, 44 (11): 2607-2610
  • 8Park A H, Bi H T, Grace J R. Reduction of electrostatic charges in gas solid fluidized beds. Chemical Engineering Science, 2002, 57 (1): 153-162
  • 9Mehrani P, Bi H T, Grace J R. Electrostatic behavior of different fines added to a Faraday cup fluidized bed. Journal of Electrostatlcs, 2007, 65 (1)z 1-10
  • 10Stow C D. Atmospheric electricity. Reportson Progress in Physics, 1969, 32:1-67

二级参考文献21

  • 1杨宝柱,王靖岱,阳永荣.乙烯气相聚合反应器中颗粒动力学的研究[J].石油化工,2004,33(12):1130-1132. 被引量:8
  • 2Gregory H. Electrostatics and Gas Phase Fluidized Bed Polymerization Reactor Wall Sheeting. Chem Eng Sci, 2006, 61 (4):104 1 -1064
  • 3Fujino M, Ogata S, Shinohara H. The Electric Potential Distribution Profile in a Naturally. Charged Fluidized Bed and Its Effects.Int Chem Eng,1985,25( 1 ) :149 - 159
  • 4Union Carbide Chemicals and Plastics Company. Process for Reducing Sheeting During Polymerization of Alpha - Olefins. US Pat Appl, US 4876320. 1989
  • 5Mobil Oil Company. Control of Static with TEOS. US Pat Appl,US 5731392. 1998
  • 6Nippon Petrochemicals Company. Method for Producing Polyolefin. US Patent Appl, US 5385991. 1995
  • 7Aida F, Wang S, Fujita M, et al. Study of the Mechanism of Space Charge Formation in Polyethylene. J Electrostatics,1997,42( 1 ) : 3 - 15
  • 8Union Carbide Chemicals and Plastics Technology Corporation.Static Control in Olefin Polymerization. US Pat Appl, US6111034. 2000
  • 9Park A H A, Bi H T, Grace J R, et al. Modeling Charge Transfer and Induction in Gas - Solid Fluidized Beds. J Electrostatics,2002,55(2) :135 - 158
  • 10Ciborowski J, Wlodarski A. On Electrostatic Effects in Fluidized Beds. Chem Eng Sci, 1962,17 (1) :23 - 32

共引文献35

同被引文献84

引证文献8

二级引证文献32

;
使用帮助 返回顶部