超临界水中煤焦油沥青轻质化的实验研究 被引量:12

Upgrading of coal-tar pitch in supercritical water
下载PDF
导出
摘要 采用间歇超临界水(supercritical water,SCW)反应器,考察了反应温度(400℃~480℃)、停留时间(1min~80min)和反应压力(25MPa~40MPa)对煤焦油沥青轻质化的影响。与常压N2热解相比,煤焦油沥青在SCW中反应后产物中的轻油质量分数高,残焦质量分数低,表明SCW可以促进煤焦油沥青的轻质化反应进行并抑制缩合反应。沥青质是煤焦油沥青在SCW中发生反应的主要组分。在440℃和34MPa时反应20min,产物中轻油的质量分数可达原料的两倍,说明煤焦油沥青在SCW中可以发生明显轻质化反应。与温度相比,压力和停留时间的影响相对较小。 Conversion of coal-tar pitch in supercritical water (SCW) was researched using a batch reactor. The effects of temperature (400 ℃ -480 ℃ ), pressure (25 MPa -40 MPa), and residence time ( 1 min - 80 min) on product composition were investigated. When compared with pyrolysis under N2 atmosphere, the conversion of asphaltene to maltene was enhanced, whereas, the formation of gas and char were restrained in SCW. Moreover the yields of high value chemicals were higher than those obtained via pyrolysis. The results suggest that SCW promotes the decomposition of coal-tar pitch into maltene and enhances the yields of high value chemicals. It is also observed that asphaltene is the main active component and it is converted to maltene, gas, and char in SCW. High temperature promotes the reactions of both asphaltene to light components and the formation of char. The results indicate that temperature appears to be the important parameter for coal tar pitch conversion, whereas, the effects of pressure and time are less significant.
出处 《燃料化学学报》 EI CAS CSCD 北大核心 2008年第1期1-5,共5页 Journal of Fuel Chemistry and Technology
关键词 煤焦油沥青 超临界水 轻质化 coal-tar pitch supercritical water upgrading
  • 引文网络
  • 相关文献

参考文献14

二级参考文献48

  • 1聂海波,沈志虹,李淑云,杨晓红.渣油催化裂化催化剂基质的改性研究[J].燃料化学学报,2001,29(z1):1-3. 被引量:14
  • 2黄谦昌.煤气化焦油加工制取汽油和柴油的研究[J].煤炭转化,1995,18(4):75-83. 被引量:17
  • 3蒂索B P 徐永元译.石油形成和分布(第二版)[M].北京:石油工业出版社,1989..
  • 4王勋章.先锋煤焦油中沥青烯与前沥青烯的裂解和高压液相加氢性质的研究[D].太原:中国科学院山西煤炭化学研究所,1988.
  • 5黄第藩,煤成油的形成和成烃机理,1995年
  • 6徐永元(译),石油形成和分布(第2版),1989年
  • 7陶著 许斌.应用差热和热失重分析对煤沥青热解过程的研究 [J].碳素,1987,(1):34-41.
  • 8Ogunsola O M, Berkowitz N. Removal of Heterocyclic S and N from Oil Precursors by Supercritical Water. Fuel, 1995, 74(10) :1485~1490
  • 9Dai Z, Hatano B, Tagaya H. Decomposition of a Polyol in Supercritical Water. Polymer Degradation and Stability, 2003, 80(2):353~356
  • 10Feng W, van der kooi H I, de Swaan A I. Phase Equilibria for Biomass Conversion Processes in Subcritical and Supercritical Water. Chemical Engineering, 2004, 98(1-2): 105~113

共引文献101

同被引文献120

引证文献12

二级引证文献36

;
使用帮助 返回顶部