NaOH亚熔盐法处理拜尔法赤泥的铝硅行为 被引量:33

Behavior of Al and Si in Bayer Red Mud Processed by NaOH Sub-molten Salt
下载PDF
导出
摘要 针对拜尔法赤泥铝/硅比偏高的问题,对NaOH亚熔盐法处理拜耳法赤泥过程中的Al,Si行为进行了研究.考察了溶出温度、碱/泥比、添加CaO等主要因素对终赤泥化学成分和物相结构的影响.结果表明,溶出温度高、碱/泥比大有利于Al2O3的回收,相应的终赤泥的铝/硅比较低.在碱/泥比6、溶出温度230℃、时间2h的条件下,氧化铝回收率可达79.22%,终赤泥的铝/硅比可降到0.39,终赤泥中的硅主要以NaCaHSiO4和Ca3(Fe0.87Al0.13)2(SiO4)1.65(OH)5.4形式存在.在处理CaO/SiO2>1.2的拜尔法赤泥时继续添加CaO并不能继续提高Al2O3的回收率. Based on the problem of higher Al2O3/SiO2 (A/S) of Bayer red mud, the separation of Al and Si in red mud from Bayer process in digestion with NaOH sub-molten salt was investigated. The effects of digestion temperature, mass ratio of alkali to red mud from Bayer process and CaO addition on the behavior of red mud in the salt were experimentally investigated. The results show that high temperature and mass ratio of alkali to red mud lead to more alumina into the aqueous phase and the decrease of A/S in brown mud. The recovery rate of Al2O3 can reach 79.22% and A/S in the brown mud is decreased to 0.39 under the conditions of mass ratio of alkali to red mud at 6, digestion temperature at 230 ℃, and digestion time for 2 h. Further study shows that Si exists in the form of NaCaHSiO4 and Ca3(Al0.13Fe0.87)2(SiOa)l.65(OH)5.4. The recovery rate can not be further raised under the condition of CaO addition in sub-molten salt process when the molar ratio of CaO to SiO2 over 1.2 in the original red mud .
出处 《过程工程学报》 EI CAS CSCD 北大核心 2008年第6期1148-1152,共5页 The Chinese Journal of Process Engineering
基金 国家重点基础研究发展规划(973)基金资助项目(编号:2007CB613500) 国家高技术研究发展计划(863)基金资助项目(编号:2006AA06Z129) 国家“十一五”科技支撑基金资助项目(编号:2006BAC02A05)
关键词 亚熔盐 拜耳法 赤泥 氧化铝 sub-molten salt Bayer process red mud alumina aluminium silicon
  • 引文网络
  • 相关文献

参考文献18

  • 1毕诗文,氧化铝生产工艺[M].沈阳:化学工业出版社,2004.32.
  • 2马淑花,郑诗礼,张懿.赤泥中氧化钠和氧化铝的回收[J].矿产综合利用,2008(1):27-31. 被引量:15
  • 3陈念怡.氧化铝生产的物理化学[M].上海:上海科学技术出版社,1962.40-49.
  • 4Vachon P, Tyagl R D, Auclalr J C, et al. Chemical and Biological Leaching of Aluminum from Red Mud [J]. Environ. Sci. Technol., 1994, 28(1): 26-30.
  • 5Atasoy A. The Comparison of the Bayer Process Wastes on the Base of Chemical and Physical Properties [J]. J. Therm. Anal. Calorim., 2007, 90(1): 153-158.
  • 6Mahata T, Sharma B P, Nair S R. Formation of Aluminum Titanate-Mullite Composite from Bauxite Red Mud [J]. Metall. Mater. Trans., 2000, 31: 551-553.
  • 7柯家骏,张帆.拜耳法赤泥水热处理的渣物相的热力学分析[J].化工冶金,1994,15(4):341-347. 被引量:7
  • 8Brunori C, Cremisini C, Massanisso P, et al. Reuse of a Treated Red Mud Bauxite Waste: Studies on Environmental Compatibility [J]. J. Hazard. Mater., 2005, 117(1): 55-63.
  • 9Cengeloglu Y, Kir E, Ersoz M. Recovery and Concentration of AI(III), Fe(III), Ti(IV) and Na(I) from Red Mud [J]. J. Colloid Interface Sci., 2001, 244(2): 342-346.
  • 10王立堂.山铝赤泥不排放的探讨[J].轻金属,1997(6):17-20. 被引量:12

二级参考文献48

共引文献60

同被引文献425

引证文献33

二级引证文献245

;
使用帮助 返回顶部