钛和锆对2219铝铜合金焊接接头组织和性能的影响 被引量:3

Effects of Ti and Zr on Microstructure and Properties of 2219 Al-Cu Alloy Weld Joint
下载PDF
导出
摘要 采用力学性能试验和组织观察的方法,研究了焊丝中添加钛和锆对2219铝铜合金惰性气体保护焊焊接接头显微组织和性能的影响。结果表明:钛和锆的组织细化作用是相容的,增加焊丝中钛和锆的含量,可促使焊缝中的粗大、方向性很强的柱状晶转变为细小的等轴晶;钛和锆同时改善了沿晶界和枝晶间分布的α(Al)-CuAl_2共晶分布形态,使其均匀分布;钛和锆可显著提高焊接接头的硬度、抗拉强度和伸长率。 Effects of Ti and Zr additions in filler wires on the microstructure and properties of metal inert gas (MIG) welding of 2219 Al-Cu alloy were investigated by means of mechanical property tests, OM and SEM. The results show that refinement effect of Ti and Zr was compatible. The coarse and oriented columnar grains reformed to fine equiaxed grains with the content increase of Ti and Zr in filler wires, which improved the morphology and distribution of α(Al)-CuAl2 eutectic along grain boundaries and interdendritic. So the microhardness, tensile strength and elongation of the weld joint was increased greatly.
出处 《机械工程材料》 CAS CSCD 北大核心 2009年第3期24-26,30,共4页 Materials For Mechanical Engineering
基金 国家"863"计划资助项目(2002AA305402)
关键词 2219铝铜合金 焊接接头 Ti Zr 2219 Al-Cu alloy weld joint
  • 引文网络
  • 相关文献

参考文献6

  • 1中国机械工程学会焊接学会.焊接手册[M].北京:机械工业出版社,2001..
  • 2KWON Y D, LEE Z H. The effect of grain refining and oxide inclusion on the fluidity of Al-4. 5Cu-0. 6Mn and A356 alloys [J]. Materials Science and Engineering A, 2003,360(2):372-376.
  • 3MOHANTY P S, GRUZLEKI J E. Mechanism of grain refinement in aluminium[J]. Acta Metallurgica et Materialia, 1995,43(5) : 2001 --2012.
  • 4VERMA R, GHOSH A K, KIM S, et al. Grain refinement and super plasticity in 5083 AI[J]. Materials Science and Engineering A, 1995,191(2) : 143--150.
  • 5MURTY B S, KORI S A, CHAKRABORTY M. Grain refinement aluminum and its alloys by heterogeneous nucleation and alloying[J]. International Materials, 2002,47 (1):3-27.
  • 6YUNIA H, FROST R H, OLSON D L. Grain refinement of A1 weld metal[J]. Welding Journal, 1989,68(7) : 280-289.

共引文献93

同被引文献25

  • 1王生,李周,尹志民,周古昕,成建国.钪锆微合金化焊丝焊接头的组织与性能[J].兵器材料科学与工程,2005,28(3):26-29. 被引量:22
  • 2田福泉,李念奎,崔建忠.超高强铝合金强韧化的发展过程及方向[J].轻合金加工技术,2005,33(12):1-9. 被引量:45
  • 3戴晓元,夏长清,马科,刘娟.Sc对Al-Zn-Mg-Cu-Zr合金铸态组织和力学性能的影响[J].中国有色金属学报,2007,17(8):1324-1329. 被引量:23
  • 4ROMETSCH P A, ZHANG Y, KNIGHT S, et al. Heat treatment of 7xxx series aluminium alloys Some recent developments[J]. Transactions ot" Nonferrous Metals Society of China,2014,24(?):2003-2017.
  • 5WILLIAMS J C, STARKE E A. Progress in structural materials for aerospace systems[J].Acta Materiala, 2003, 51 (19) : 5775-5799.
  • 6OCENASEK V, SLAMOVA M. Resistance to recrystallization due to Sc and Zr addition to A1-Mg alloys [J]. Materials Characterization, 2001,47 (2) .. 157-162.
  • 7ROBSON J D, PRANGNELL P B. Modelling Ala Zr dispersoid precipitation in muiticomponent alumininm alloys[J].Materials Science and Engineering A, 2003,352 (1/2) : 240-250.
  • 8DORWARD R C. Precipitate coarsening during over ageing of A1-Zn-Mg-Cu alloys[J]. Material Science and Technology, 1999, 15(10)~ 1133-1138.
  • 9ROMETSCH P A, ZHANG Y, KNIGHT S, et al. Heat treatment of 7xxx series aluminium alloys-some recent developments[J]. Trans Nonferrous Mel Soc China, 2014, 2.1 (7): 2003-2017.
  • 10JAMES C, WILI.IAMS J C, STARKE E A. Progress in structural materials for aerospace systems[J]. Acla Materiala, 2003, 51(19): 5775-5799.

引证文献3

二级引证文献2

;
使用帮助 返回顶部