微弧等离子喷涂制备莫来石/金属复合热障涂层 被引量:4

Mullite/metal composite thermal barrier coating deposited by micro-plasma spraying
下载PDF
导出
摘要 运用微弧等离子喷涂制备了莫来石/金属复合热障涂层.研究了涂层的微观结构、结合强度、隔热性能和抗热震性能.复合涂层结构为莫来石颗粒被"包裹"在金属层片状结构中;涂层的结合强度大于30 MPa.随着涂层中莫来石含量的增加,涂层的隔热性能有所提高,随涂层表面温度的升高,涂层的隔热温度也不断提高,涂层的最高隔热温度为125℃.1 150℃的水淬热震试验表明,基体变形是导致涂层失效的重要原因之一,随着涂层中莫来石含量的增加,涂层的抗热震次数先增加后减小,粉末中莫来石含量为40%的涂层的抗热震性能最好,抗热震次数最多为72次. Mullite/metal thermal barrier coatings(MMCs) have been sprayed by micro-plasma spraying.The microstructure,bond strength,thermal barrier insulation and thermal shock resistance of the coatings have been investigated.The microstructure of MMC shows that mullite particles are surrounded by the metal lamellar structure.The average bond strength of the coatings is more than 30 MPa.The thermal barrier insulation of the coatings is improved with the increasing of surface temperature and the mullite fraction.At surface temperature of 1 175 ℃,the maximum thermal barrier insulation of coating is 125 ℃ with 70% mullite in the powder.The thermal shock resistance test,in which the specimens are heated up to 1 150 ℃ and then quenched in the water,shows that one of the main reasons for coating failure is substrate deformation.The thermal shock resistance of coatings is increased firstly,and decreased in succession quickly with the mullite fraction increasing,and the peak value of the thermal shock resistance is 72 times with 40% mullite fraction in the powder.
出处 《焊接学报》 EI CAS CSCD 北大核心 2009年第5期85-88,92,共5页 Transactions of The China Welding Institution
关键词 热障涂层 微弧等离子喷涂 莫来石 复合涂层 抗热震性能 thermal barrier coatings(TBCs) micro-plasma spray mullite composite coating thermal shock resistance
  • 引文网络
  • 相关文献

参考文献4

二级参考文献24

共引文献60

同被引文献56

  • 1李柳生,平增福.红柱石的莫来石化[J].硅酸盐通报,2006,25(1):34-36. 被引量:13
  • 2关耀辉,徐杨,郑仲瑜,佟晓辉.等离子喷涂纳米FeS涂层的摩擦磨损性能研究[J].摩擦学学报,2006,26(4):320-324. 被引量:15
  • 3魏琪,任春岭,崔丽,栗卓新.电弧喷涂铝基涂层耐腐蚀性能[J].焊接学报,2006,27(11):5-8. 被引量:7
  • 4宁成云,王迎军,赵娜如,陈晓峰,叶建东,吴刚,陈虎,郑华德.HA/ZrO2功能梯度涂层中羟基磷灰石的超微结构分析[J].中国材料科技与设备,2007,4(3):61-64. 被引量:5
  • 5Rohan P, Neufuss K, Matcjlcek J, et al. Thermal and Mechanical Properties of Cordierite, Mullite and Steatite Produced hy Plasma Spraying[J]. Ceramics International, 2004, 30: 597-603.
  • 6Garcia E, Mesquita-Guimaraes J, Miranzo P. et al. Mullile and Mullite/ZrO2 7wt.% Y2O3 Powders for Thermal Spra ying of Environmental Barrier Coatings[J]. Journal of Ther mal Spray Technology, 2010. 19 (1/2) : 286- 293.
  • 7Lee K N. Current Status of Environmental Barrier Coatings for Si based Ceramics[J]. Surface and Coatings Technology, 2000, 33/34:1- 7.
  • 8Das S, GhoshS, Pandit A. et al. Processing and Characterisation of Plasma Sprayed Zirconia alumina mullite Composite Coating on a Mild steel Substrate[J]. Journal of Materials Science Letters, 2005,18(40):5087 -5089.
  • 9Seifert S, Litovsky E, Kleiman J I, et al. Thermal Resistance and Apparent Thermal Conductivity of Thin Plasma sprayed Mullite Coatings[J]. Surface and Coatings Technology, 2006. 200: 3404-3410.
  • 10Rarnaswamy P, Seetharamu S, Varma K B R, et al. Thermal Shock Characteristics of Plasma Sprayed Mullite Coatings [J]. Journal of Thermal Spray Technology, 1998, 7(4): 497 -504.

引证文献4

二级引证文献39

;
使用帮助 返回顶部