The chemical conversion coating was formed on Mg alloy for low cost and harmlessness in environment by using the colloidal silica as the main component.The film formed at 298 K was thick,which was thought to be the combination of Si and O.In salt spray test,the ratio of black rust on the specimen that did not conducted chemical conversion treatment was five times or more than those of the chemical conversion treated specimen.The film of chemical conversion coating produced by alkali treatment process was thinner than the specimen produced in basic chemical conversion treatment solution.
The chemical conversion coating was formed on Mg alloy for low cost and harmlessness in environment by using the colloidal silica as the main component. The film formed at 298 K was thick, which was thought to be the combination of Si and O. In salt spray test, the ratio of black rust on the specimen that did not conducted chemical conversion treatment was five times or more than those of the chemical conversion treated specimen. The film of chemical conversion coating produced by alkali treatment process was thinner than the specimen produced in basic chemical conversion treatment solution.
出处
《中国有色金属学会会刊：英文版》
EI
CSCD
2009年第4期892-897,共6页
Transactions of Nonferrous Metals Society of China