微弧等离子喷涂制备空心莫来石隔热涂层研究 被引量:3

Micro-plasma Sprayed Hollow Mullite Thermal Barrier Coatings
下载PDF
导出
摘要 采用微弧等离子喷涂方法制备了空心微珠莫来石隔热涂层。研究了涂层的结合强度、隔热性能和抗热震性能。实验结果表明:拉伸断裂发生在莫来石涂层内,涂层的平均结合强度约为5.63MPa;稳态测量涂层隔热温度,当涂层表面温度为400℃~800℃时,涂层的隔热温度变化范围为11.5℃~40℃;热震温度为400℃~800℃间隔100℃时,涂层的抗热震次数分别为165、135、117、81和34次;涂层先从试样边沿开始剥落,并呈加速剥落的趋势。涂层失效主要原因是由于热震过程中残余应力积聚造成的。 The hollow mullite thermal barrier coatings were deposited by Micro-plasma Spraying technique. The bond strength, thermal barrier capability and the anti-thermal shock ability of the coating were tested. The tested results show that the average bond strength of the coating is 5.63 MPa, the fracture begins in the top coating; The thermal barrier of the coatings goes up form 11.5 ℃ to 40 ℃ under the surface temperature going up form 400 ℃ to 900 ℃ conditions in which the steady-state test is employed; the anti-thermal shock times are 165, 135, 117, 81, and 34 when the test temperature is between 400 ℃ and 800 ℃ with interval of 100 ℃ ; the initial spallation of the mullite coating occurs at the edge of the specimen, and its speed increases at the end of thermal shock life. The main failure reason of the coatings is the thermal residual stress accumulated during the thermal shock test.
出处 《兵工学报》 EI CAS CSCD 北大核心 2009年第8期1108-1113,共6页 Acta Armamentarii
关键词 材料表面与界面 微弧等离子喷涂 莫来石 隔热涂层 结合强度 抗热震性能 suface and interface for the material micro-plasma spray mullite thermal barrier coatings bond strength thermal shock resistant
  • 引文网络
  • 相关文献

参考文献11

二级参考文献62

共引文献170

同被引文献31

  • 1张敬国,刘金炎,蒋显亮.碳化钨/钴热喷涂粉末和涂层的研究进展[J].功能材料,2005,36(3):332-334. 被引量:11
  • 2陈飞,周海,吕涛,刘凯.不锈钢表面等离子喷涂梯度涂层耐蚀性能的研究[J].金属热处理,2006,31(11):22-24. 被引量:2
  • 3Miller R A. Thermal barrier coatings for aircraft engines: History and directions[J]. J Thermal Spray Techn, 1997,6 (1):35.
  • 4Lee IK N. Current status of environmental barrier coatings for Si based ceramics[J].Surf Coat Teehn, 2000(133-134) : 1.
  • 5Mab T, Mazdiyasni K J. Mechanical properties of mullite[J].J Am Ceram Soc,1983,66(10) :699.
  • 6曹雪强.热障涂层材料[M].北京:科学出版社,2007:161.
  • 7Oberste Berghaus J, Marple B R. High-velocity oxy-fuel (HVOF) suspension spraying of mullite coatings[J]. J Thermal Spray Techn,2008,17(5 -6) :671.
  • 8Ramaswamy P, Seetharamy S,Varma K B R, et al. Thermal shock characteristics of plasma sprayed mullite coatings[J].J Thermal Spray Techn, 1998,7 (4) : 497.
  • 9Cano C, Garcia E, Fernandes A L, et al. Mullite/ZrO2 coa tings produced by {lame spraying[J]. J Eur Ceram Soc, 2008,28(11) :2191.
  • 10Lee K N, Miller R A, Jacobson N S. New generation of plasma sprayed mullite coatings on silicon carbide[J]. J Am Ceram Soc, 1995,78(3): 705.

引证文献3

二级引证文献7

;
使用帮助 返回顶部