大气等离子喷涂制备莫来石涂层的性能 被引量:3

Characteristics of Mullite Coatings Prepared by Air Plasma Spraying
下载PDF
导出
摘要 采用大气等离子喷涂制备莫来石涂层,对涂层进行了热震试验。以OLYCIA m3图像分析软件测定涂层孔隙率,以MH-5-VM型显微硬度仪测定涂层硬度,依照ASTMC633-79标准测定涂层结合强度,以X射线衍射(XRD)和扫描电镜(SEM)表征涂层的相组成和微观形貌。结果表明,莫来石涂层主要由变形颗粒、未熔融粉末及少量孔隙组成,涂层中没有微观裂纹;涂层中含有莫来石晶体和部分非晶态玻璃相;热震过程中,涂层中的非晶转变为晶态莫来石,同时伴随应力释放,导致涂层出现微观裂纹。 The mullite coatings were prepared by air plasma sprayed. The as-sprayed coating were carried out thermal shock experiment. The porosity and microhardness were measured by OLYCIA m3 image analysis software and MH-5-VM microhardness tester, respectively. The bond strength of mullite coatings were determined according to ASTM C633-79 standard. The composition and morphology of the mullite coatings were examined by X-ray diffraction (XRD) and scanning electron microscope(SEM). The results show that as-sprayed coating includes splats grains, partially melted powders and a few pores. The microcracks do not appear in the coating. The as-sprayed coating is largely crystal mullite and only a small quantity of amorphous phase. During thermal shock experiment, amorphous phase in coating changes to crystal mullite and gives rise to stress, leading to microcracks.
出处 《材料导报》 EI CAS CSCD 北大核心 2011年第2期36-39,共4页 Materials Reports
基金 国家自然科学基金委创新研究群体科学基金资助项目(50421502)
关键词 大气等离子喷涂 莫来石涂层 热震试验 非晶 air plasma spray, mullite coatings, thermal shock experiment, amorphous
  • 引文网络
  • 相关文献

参考文献13

二级参考文献122

共引文献233

同被引文献28

  • 1尚书勇,梅丽,李兰英,印永祥,戴晓雁.等离子体法制备超细粉体氮化铝的研究[J].化工新型材料,2004,32(7):8-10. 被引量:5
  • 2蒋显亮,M.BOULOS.Induction plasma spheroidization of tungsten and molybdenum powders[J].中国有色金属学会会刊:英文版,2006,16(1):13-17. 被引量:34
  • 3胡鹏,闫世凯,袁方利,白柳杨,李晋林,陈运法.Effect of Plasma Spheroidization Process on the Microstructure and Crystallographic Phases of Silica, Alumina and Nickel Particles[J].Plasma Science and Technology,2007,9(5):611-615. 被引量:8
  • 4Chawla K K. Interface engineering in mullite fiber/mullite matrix composites[J]. J Eur Ceram Soc,2008,28 (2) :447.
  • 5Kriven W M, et al. Toughening of mullite/cordierite lami- nated composites by transformation weakening of beta-cris- tobalite interphases [J]. J Am Ceram SOc, 2005,88(6) : 1521.
  • 6Song G M, Zhou Y,Sun Y. Modeling of fiber toughening in fiber-reinforced ceramic composites [J]. Ceram Int, 1999,25 (3):257.
  • 7Pan Wei, Gong Jianghong. Microstructures and multi-toug- hening of ZrOz nano-micron fibers self-toughening AI2 03 ce- ramics from in situ growth in the melts produced by com- bustion synthesis [J]. Key Eng Mater, 2007,336-338:2257.
  • 8Nourbakhsh S, Sahin O, Rhee W H, et al. Microstructural characterization of a zirconia-toughened alumina fiber rein- forced niobium aluminide composite [J]. Acta Metall Ma- ter, 1992,40 (2) : 285.
  • 9Hummer E, Lu X, Rettelbach Th, et al. The application of the single-edge notched beam to fracture toughness testing of ceramics [J]. J Test Evaluat, 1974,2(6) : 503.
  • 10Chiang Yih-Cherng. On fiber debonding and matrix cracking in fiber-reinforced ceramics[J]. Compos Sci Techn, 2001, 61 (12) : 1743.

引证文献3

二级引证文献6

;
使用帮助 返回顶部