摘要
采用抽真空层压法制备真丝织物/PE膜复合材料;利用色差分析法,优选丝纤维与PE膜复合体积的配比。在PE膜与真丝织物体积配比为5∶1,复合材料厚度为0.3 mm的条件下,通过正交试验,以拉伸强力、顶破强力和撕裂强力为指标,优化出其热压成形工艺条件为热压温度145℃、热压压力3 MPa、热压时间4 min。
This paper discusses the process of decorative composites prepared by silk fabric/PE film which is made by hot pressing method.Using color-difference analysis,optimization for volume ratio of the silk fabrics and PE film was given out.When the requirements are 5：1 of volume ratio for PE film and silk fabrics,0.3 mm of thickness,the optimal performances of prepared composites which compared with the silk fabric for tensile properties,bursting properties and tearing properties are 145 ℃ of temperature,3 MPa of pressure and 4 min of time by Orthogonal test.