SiO_2气凝胶结构及其热学特性研究 被引量:18

Structure and Thermal Properties of SiO_2 Aerogels
下载PDF
导出
摘要 以正硅酸四乙酯为硅源, 通过溶胶-凝胶及超临界干燥过程制备了 SiO2 气凝胶。用透射电镜、扫描电镜以及孔径分布仪对其结构进行了表征, 并用稳态热线法对其热学特性进行了测试。结果表明: SiO2 气凝胶的孔洞大小分布在 5~70nm , 峰值在 20nm 附近, 组成网络的胶体颗粒为 5~10nm ; 热学测试结果显示SiO2 气凝胶 (100kgm - 3 ) 的热导率在常温常压下为 0.0125Wm - 1 K- 1 。 Nano porous SiO 2 aerogel insulation were prepared via sol gel process using tetraethoxysilane (TEOS) as the precursor and followed by ethanol supercritical drying TEM, SEM and pore size distribution techniques were used to characterize the morphology and pore structure of the silica aerogels The thermal conductivity measurement of the silica aerogels was determined using the transient hot wire technique The results show that the pore size is 5~70 nm, the average pore size (BJH) is about 20 nm, the size of the particles is 5~10nm while the thermal conductivity of the silica aerogel (100kgm -3 ) is 0 0125 Wm -1 K -1 at room temperature and 1 atm
出处 《材料工程》 EI CAS CSCD 北大核心 1999年第12期23-25,共3页 Journal of Materials Engineering
基金 国家自然科学基金! (59802007) 863 基金! (863-416-3-9)
关键词 SiO2气凝凝 溶胶-凝胶 保温隔热材料 热学特性 SiO 2 aerogel sol gel super critical drying thermal conductivity
  • 引文网络
  • 相关文献

参考文献7

  • 1王珏.-[J].物理,1995,24:47-51.
  • 2邓忠生 魏建东 等.-[J].原子能科学技术,1999,33(4):29-29.
  • 3王珏,吴卫东,沈军,陆献平.热导率的动态热线法测量系统[J].物理,1995,24(1):47-51. 被引量:8
  • 4邓忠生,原子能科学技术,1999年,33卷,4期,29页
  • 5Deng Zhongsheng,J Non Cryst Solids,1998年,225卷,101页
  • 6Wang Jue,Nanostruct Mater,1998年,10卷,6期,909页
  • 7Wang J,J Non Cryst Solids,1995年,186卷,296页

二级参考文献2

共引文献8

同被引文献155

引证文献18

二级引证文献201

相关主题

;
使用帮助 返回顶部