金属材料应力腐蚀裂纹的探讨 被引量:4

Discussion of Metal Material Stress Corrosion Crack
下载PDF
导出
摘要 金属被环境介质的化学以及电化学作用而受破坏过程即腐蚀。根据工程实情,对应力腐蚀裂纹的形成等问题展开研究,对设计中怎样更有效地实施措施以防止金属材料应力腐蚀的现象发生以及在生产实践中怎样处理金属材料应力腐蚀裂纹的问题进行探究。 Corrosion means the process which metal is damaged by the environmental medium through chemical and electrochemical action. According to the actual project situation, with the help of the study of stress corrosion crack issues, we have explored the methods about how to deal with such problems effectively and prevent the crack in the design.
作者 陶勇
出处 《中国教育技术装备》 2013年第6期131-131,134,共2页 China Educational Technology & Equipment
关键词 金属材料 应力腐蚀 裂纹 Metal material stress corrosion crack
  • 引文网络
  • 相关文献

参考文献4

二级参考文献9

  • 1Yusa N, Chen Z, Miya K. Quantitative profile evaluation of natural crack in steam generator tube from eddy current signals [ J ]. Int J Appl Electromagn Mech, 2000,12(3-4) : 139- 150.
  • 2Cheng W, Kanemoto S, Komura I. Depth sizing of partial contact SCC from ECT signals[J]. NDT&E Int,2006,39(5) :374-383.
  • 3Yusa N, Chen Z, Miya K. Large-scale parallel computation for the reconstruction of natural stress corrosion cracks from eddy current testing signals[J]. NDT&E Int,2003,36(7) :449-459.
  • 4Yusa N, Cheng W Y, Chen Z M. Generalized neural network approach to eddy current inversion to the analysis of real cracks[J]. NDT&E Int, 2002, 35 (8): 609-614.
  • 5Yusa N, Miya K. Discussion on the equivalent conductivity and resistance of stress corrosion cracks in eddy current simulations[J]. NDT&E Int, 2009,42 (1):9- 15.
  • 6Yusa N, Hashizume H. Evaluation of stress corrosion cracking as a function of its resistance to eddy currents [J]. Nuclear Engineering and Design, 2009,239 (12) : 2713-2718.
  • 7Yusa N, Huang H, Miya K. Numerical evaluation of the ill-posedness of eddy current problems to size cracks[J]. NDT&E Int,2007(40):185-191.
  • 8Wang L, Chen Z, Lu T J. Sizing of long stress corrosion crack from 2D ECT signals by using a multisegment inverse analysis strategy[J]. Int J Appl Electromagn Mech,2008,28(1-2) :155-161.
  • 9Norton S J, Bowler J R. Theory of eddy current inversion[J]. J Appl Phys, 1993,73 (2) : 501- 512.

共引文献2

同被引文献24

引证文献4

二级引证文献12

;
使用帮助 返回顶部