摘要
通过溶胶-凝胶(Sol-Gel)技术制备出比表面积高、孔径分布窄的锐钛型二氧化钛粉末,并用热重分析、X-射线衍射、比表面仪、透射电镜、元素分析、红外光谱等方法进行表征。以甲苯气相光氧化降解为模型反应,对其催化性能进行评价并与商业化产品Degussa P-25 进行比较。实验结果表明,比表面积为128m 2/g、孔径为6.81nm 、晶粒尺寸为8.34nm 、团聚体为200~300nm 的锐钛型二氧化钛粉体具有良好的催化活性。
High surface area、narrow pore radius distribution anatase TiO 2 was prepared by Sol Gel method and characterized by TG、XRD、BET、TEM、EMA and IR. Toluene photocatalytic oxidation was used as a model reaction to waluate the activity and mineralizing selectivity of the catalysts and compared with that of commercially available TiO 2 powders Degussa P 25. The results showed that 128m 2/g surface area、6.81nm pore radius、8.34nm crystallite size、200~300nm grain aggregates anatase TiO 2 powders got better photocatalysis activity.