摘要
In order to improve the service life of corundum lin- ing.for induction Jitrnace, corundum dry ramming mix was prepared using brown corundum, fu.sed magnesia, and α-Al2O3 micropowder as main starting materials, mul the it!fluence of α-Al2O3 micropowder additions （0, 1% , 2%, and 3%, in mass） on properties of corundum dry ramming re.ix was investigated. The results show that after heat treating at 1 600 ~C , with the in-crease of α-Al2O3 addition, the permanent change in di- mensions on heating of the specimens decreases firstly and then increases, bulk density increases, apparent po- rosity decreases, and the crushing strength declines first- Iv and then enhances; when the addition of α-Al2O3 is 2 mass% , the termanent change in dimensions on heating of the specimens i.s relatively small and the crushing .strength decrease.s to 22.8 MPa. The XRD attd SEM reults show that after .firing at 1 600 for 3 h sin, all granular magnesium aluminate spinel form. and is welldistributed, which enhances the density.
In order to improve the service life of corundum lin- ing.for induction Jitrnace, corundum dry ramming mix was prepared using brown corundum, fu.sed magnesia, and α-Al2O3 micropowder as main starting materials, mul the it!fluence of α-Al2O3 micropowder additions （0, 1% , 2%, and 3%, in mass） on properties of corundum dry ramming re.ix was investigated. The results show that after heat treating at 1 600 ~C , with the in-crease of α-Al2O3 addition, the permanent change in di- mensions on heating of the specimens decreases firstly and then increases, bulk density increases, apparent po- rosity decreases, and the crushing strength declines first- Iv and then enhances; when the addition of α-Al2O3 is 2 mass% , the termanent change in dimensions on heating of the specimens i.s relatively small and the crushing .strength decrease.s to 22.8 MPa. The XRD attd SEM reults show that after .firing at 1 600 for 3 h sin, all granular magnesium aluminate spinel form. and is welldistributed, which enhances the density.