AP1000施工现场典型腐蚀问题探讨与预防 被引量:5

Prevention and Discussion for Typical Corrosion Problems at the AP1000 Construction Site
下载PDF
导出
摘要 本文根据AP1000施工现场的腐蚀现象,对典型的钢结构、焊缝和设备等腐蚀现象进行了总结,基于腐蚀的表现形式,分析了引起施工现场材料和设备腐蚀的主要原因,并对腐蚀现象的形成机理进行了分析,从理论和施工实践的角度给出了预防性措施。 On the basis of corrosion phenomena appeared on the APIO00 construction site, this article summarized the typical corrosion phenomena on the steel structure, weldjoints and equipments. The main causes that lead to materials and equipments corrosion on site have been analysed based on the corrosion patterns, so as the formation mechanism of the corrosion. Anti corrosion measures have also been proposed from theoretical and construction practical point of view.
作者 魏小宝 张琰
出处 《全面腐蚀控制》 2014年第1期44-48,共5页 Total Corrosion Control
关键词 AP1000 施工现场 海洋大气腐蚀 尘土腐蚀 AP1000 construction site sea atmosphere corrosion dust corrosion
  • 引文网络
  • 相关文献

参考文献8

二级参考文献85

共引文献183

同被引文献34

  • 1张曾生,熊金平,左禹.无机富锌漆研究及进展[J].现代涂料与涂装,2007,10(2):16-20. 被引量:16
  • 2韩文礼,徐忠苹,王雪莹,李爱贵.紫外线对有机涂层的破坏机理及应对措施[J].石油工程建设,2007,33(2):18-20. 被引量:25
  • 3高国,梁成浩.气相缓蚀剂的研究现状及发展趋势[J].中国腐蚀与防护学报,2007,27(4):252-256. 被引量:25
  • 4方小鹏,沈文荣,孙克彬,等.APl000核电项目模块化施工建造管理研究[C]//中国核科学技术进展报告-中国核学会2009年学术年会论文集(第1卷).北京:中国核工业集团公司.2009.
  • 5胡梅,杨光雄,顾肇杰,等.防霉防护技术在水性涂料中的应用[C]//第九届全国防霉防菌技术研讨及产品交流会论文集.北京:中化化工科学技术研究总院,2011.
  • 6刘新.海上风电场的防腐涂装[J].材料保护,2011,44(增刊):20-23.
  • 7林诚格.非能动安全先进核电厂APl000[M].北京:原子能出版社,2010:190-193.
  • 8Timothy S, Andreychek. Protective Coatings in 21 st Centu- ry Nuclear Plants [ J ]. Paint & Coating Industry, 2009 (12) :52.
  • 9US. NRC. RG 1.54, Service level I, II and III protective eoatings applied to nuclear power plants [ R ]. Washing- ton:US NRC ,2000.
  • 10百度百科[OB/L].环氧面漆.

引证文献5

二级引证文献11

;
使用帮助 返回顶部