水性丙烯酸树脂/氧化石墨烯抗静电涂层的制备及性能研究

Preparation and Properties Characterization of Waterborne Acrylic Resin/Graphene Oxide Antistatic Coating

采用水性丙烯酸树脂为基料,考察了氧化石墨烯含量对抗静电涂层性能的影响。结果表明,当氧化石墨烯质量分数为3.5%时,涂层的体积电阻率达到2.604×107Ω·cm,冲击性能和耐老化性能均最佳。

Using waterborne acrylic resin as the basic material, the influence of graphene oxide content on the antistatic coating performance was investigated in this paper. Experimental results showed that the volume resistivity of the coating with graphene oxide content of 3.5% was 2.604×10^7 Ω·cm with the best impact performance and aging resistance.