高性能氧化锆陶瓷最优工艺研究 被引量:5

Research on Optimal Process of High Performance Zirconia Ceramics
下载PDF
导出
摘要 通过共沉淀法制备了高性能Y-ZrO2陶瓷,研究了等静压压力、烧结温度和保温时间对氧化锆陶瓷相对密度、抗弯强度、硬度和断裂韧性的影响。结果表明,随等静压压力的增大,相对密度和抗弯强度增大,硬度和断裂韧性变化不大;随烧结温度的升高和保温时间的延长,相对密度和抗弯强度先增大后减小,硬度和断裂韧性先增大后略有下降。在等静压压力200MPa、1450℃烧结、保温2h时获性能最高的氧化锆陶瓷材料。 The high performance Y-ZrO2 ceramics were prepared by co-precipitation. The effects of isostatic pressure, sintering temperature and soaking time on the relative density, bending strength, hardness and fracture toughness of zirconia ceramics were studied. The results showed that the relative density and bending strength increased with the increase of isostatic pressure, while the hardness and fracture toughness changed little. With the increase of sintering temperature and soaking time, the relative density and bending strength first increased and then decreased, while the hardness and fracture toughness first increased and then slightly decreased. Zirconia ceramic materials with the highest performance were obtained under the isostatic pressure of 200 MPa, by sintering at 1450°C and soaking for 2 hours.
作者 杜亚男 范立坤 DU Yanan;FAN Likun(Shanghai Key Laboratory of Engineering Materials Application and Evaluation,Shanghai Research Institute of Materials,Shanghai 200437,China)
出处 《中国陶瓷工业》 CAS 2019年第6期1-4,共4页 China Ceramic Industry
关键词 Y-ZrO2陶瓷 等静压压力 烧结温度 保温时间 性能 Y-ZrO2 ceramics isostatic pressure sintering temperature soaking time performance
  • 引文网络
  • 相关文献

参考文献3

二级参考文献43

共引文献61

同被引文献59

引证文献5

二级引证文献3

;
使用帮助 返回顶部