Heteroatom dopant strategy triggered high-potential plateau to non-graphitized carbon with highly disordered microstructure for high-performance sodium ion storage

Non-graphitized carbon(NGC)has been extensively utilized as carbonaceous anode in sodium-ion batteries(SIBs).However,more optimization to achieve competitive capacity and stability is still challenging for SIBs.In the study,the dopant strategy is utilized to construct nitrogen/sulfur-doped non-graphitized carbon(N-NGC or S-NGC)shell decorated on three-dimensional graphene foam(GF)as a self-support electrode.The highly disordered microstructures of heteroatom doped carbons are produced by applying a low-temperature pyrolysis treatment to precursors containing nitrogen and sulfur.The DFT calculations of Na-ion adsorption energies at diverse heteroatom sites show marginal-S,pyrrolic N and pyridinic N with more intensive Na-ion adsorption ability than middle-S,C=O and pristine carbon.The N-NGC with dominant small graphitic regions delivers adsorption ability to Na-ion,while the S-NGC with significant single carbon lattice stripes demonstrates redox reaction with Na-ion.Evidently,in comparison with only adsorption-driven slope regions at high potential for N-NGC,the redox reaction-generated potentialplateau enables non-graphitized S-NGC superior discharge/charge capacity and cycle-stability in the slope region.This work could provide deep insight into the rational design of non-graphitized carbon with rich microstructure and composition.