Characterization and Magnetic Properties of Cobalt Nano-Particles Prepared by Metal Vapor Synthesis Technique

Characterization and Magnetic Properties of Cobalt Nano-Particles Prepared by Metal Vapor Synthesis Technique
下载PDF
导出
摘要 The metal vapor synthesis technique was employed to prepare Co nanoparticles. The characteristics and properties of the particles were studied by transmission electron microscopy, X-ray diffraction, temperature-programmed desorption, chemisorption and magnetic measurements. The experimental results showed that the particle size of Co powders depended on the initial Co concentration in the toluene matrix, reaching average crystallite diameter of 1.5 nm for the highest concentration (6.4 at. pct) investigated. The particles with size of 10 nm exist, due to the agglomerates of microcrystallites. The Co particles were surrounded by a thin carbonaceous layer formed due to toluene decomposition on cocondate melt-down and subsequent warming to room temperature. The carbonaceous layer was composed primarily of C1 fragments. The Co powders demonstrated ferromagnetic behavior. The metal vapor synthesis technique was employed to prepare Co nanoparticles. The characteristics and properties of the particles were studied by transmission electron microscopy, X-ray diffraction, temperature-programmed desorption, chemisorption and magnetic measurements. The experimental results showed that the particle size of Co powders depended on the initial Co concentration in the toluene matrix, reaching average crystallite diameter of 1.5 nm for the highest concentration (6.4 at. pct) investigated. The particles with size of 10 nm exist, due to the agglomerates of microcrystallites. The Co particles were surrounded by a thin carbonaceous layer formed due to toluene decomposition on cocondate melt-down and subsequent warming to room temperature. The carbonaceous layer was composed primarily of C1 fragments. The Co powders demonstrated ferromagnetic behavior.
出处 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 2003年第5期422-424,共3页 材料科学技术(英文版)
关键词 Metal vapor synthesis Cobalt nanoparticles MAGNETIZATION Metal vapor synthesis, Cobalt nanoparticles, Magnetization
  • 引文网络
  • 相关文献

参考文献1

;
使用帮助 返回顶部