摘要
The effect of relaxation after finished rolling on structures and properties of four microalloyed steel with different content of Nb and Ti was investigated. By alloy designing and control rolling + relaxation-precipitation-control phase trail storm ati on (RPC) process, a new 800 MPa grade HSLA plate steel could be obtained, the microstructure is composite ultra-fine lath bainite/martensite. The tempering process and mechanical properties of this kind of HSLA steel were investigated. The yield strength can achieve 800 MPa, and the ductility and impact toughness is satisfied.
The effect of relaxation after finished rolling on structures and properties of four microalloyed steel with different content of Nb and Ti was investigated. By alloy designing and control rolling + relaxation-precipitation-control phase trail storm ati on (RPC) process, a new 800 MPa grade HSLA plate steel could be obtained, the microstructure is composite ultra-fine lath bainite/martensite. The tempering process and mechanical properties of this kind of HSLA steel were investigated. The yield strength can achieve 800 MPa, and the ductility and impact toughness is satisfied.