摘要
The 08 Al steel sheets were hot dip ped into Zn - Mn bath with 0 1 % Mn and 0 2 % Mn at600 ～420 ℃ bath tem perature , and then w ere treated in different w ays . The after - treat ments include cooling in the air at room tem perature directly , holding at the upper part of thehot dip galvanizing furnace for 60 s an d then holding at 510 ±10 ℃for 90 s . The results in dicated that blue , yellow , and purple , w hose coloration varied with the co m position an d thetem perature of bath and the w ays of after - treat ment . Finally , the mechanism of coloredzinc coating w as discussed .
The 08 Al steel sheets were hot dip ped into Zn - Mn bath with 0 1 % Mn and 0 2 % Mn at600 ～420 ℃ bath tem perature , and then w ere treated in different w ays . The after - treat ments include cooling in the air at room tem perature directly , holding at the upper part of thehot dip galvanizing furnace for 60 s an d then holding at 510 ±10 ℃for 90 s . The results in dicated that blue , yellow , and purple , w hose coloration varied with the co m position an d thetem perature of bath and the w ays of after - treat ment . Finally , the mechanism of coloredzinc coating w as discussed .