Study on the Dissolution of Dusts in Glutamic Acid

This article describes the characteristics of natural dusts, artificial dusts and industrial dusts, such as mineral phases, chemical components, morphological observation and size. Quartz and calcite are the main phases of natural dusts and industrial dusts with high SiO2, CaO and low K2O, Na2O on the chemical composition. Natural dusts are mainly irregular shaped and some particle aggregation made of small dusts on the surface of large dust. Industrial dusts are globular and blob-like, but artificial dusts are columnar and fibrous. The fine particles are mainly in the range of 0.3-5 μm,of which the dusts of less than 5 μm are over 99%.The dissolution and electrochemical action of dusts in glutamic acid liquor at the simulated human body temperature (37 ℃) in 32 hours were investigated. The changes of pH values and electric conductivity of those dusts were similar, increased slowly in first 8 hours, and then the pH values increased rapidly. The total amount of dissolved ions of K, Ca, Na, Mg was 35.4-429 mg/L, particularly Ca was maximal of 20-334 mg/L. The total amount of dissolved ions of Fe, Zn, Mn, Pb, Ba was 0.18-5.59 ppm and the Al, Si was 3.0-21.7 mg/L. Each element dissolved rapidly relatively in first 16 hours. The relative solubility order of dusts in glutamic acid are: wollastonite > serpentine > sepiolite, the cement plant industrial dusts > power plant industrial dusts, and natural dusts have similar solubility. The wollastonite and power plant industrial dusts have highest solubility, which have high content of CaO; this shows there are a poorer corrosion-resisting ability and lower bio-resistibility. Sepiolite and cement plant industrial dusts have lowest solubility, which have high content of SiO2; this shows there are a higher corrosion-resisting ability and stronger bio-resistibility.

This article describes the characteristics of natural dusts, artificial dusts and industrial dusts, such as mineral phases, chemical components, morphological observation and size. Quartz and calcite are the main phases of natural dusts and industrial dusts with high SiO2, CaO and low K2O, Na2O on the chemical composition. Natural dusts are mainly irregular shaped and some particle aggregation made of small dusts on the surface of large dust. Industrial dusts are globular and blob-like, but artificial dusts are columnar and fibrous. The fine particles are mainly in the range of 0.3-5 μm,of which the dusts of less than 5 μm are over 99%.The dissolution and electrochemical action of dusts in glutamic acid liquor at the simulated human body temperature (37 ℃) in 32 hours were investigated. The changes of pH values and electric conductivity of those dusts were similar, increased slowly in first 8 hours, and then the pH values increased rapidly. The total amount of dissolved ions of K, Ca, Na, Mg was 35.4-429 mg/L, particularly Ca was maximal of 20-334 mg/L. The total amount of dissolved ions of Fe, Zn, Mn, Pb, Ba was 0.18-5.59 ppm and the Al, Si was 3.0-21.7 mg/L. Each element dissolved rapidly relatively in first 16 hours. The relative solubility order of dusts in glutamic acid are: wollastonite > serpentine > sepiolite, the cement plant industrial dusts > power plant industrial dusts, and natural dusts have similar solubility. The wollastonite and power plant industrial dusts have highest solubility, which have high content of CaO; this shows there are a poorer corrosion-resisting ability and lower bio-resistibility. Sepiolite and cement plant industrial dusts have lowest solubility, which have high content of SiO2; this shows there are a higher corrosion-resisting ability and stronger bio-resistibility.