摘要
Phase structures, the transport ana magnetic properties of the Perovskite-type manganite （La0.8-x CexSr0.2）0.97 MnO3（x = 0 - 0. 26） prepared by La2O3 containing CeO2 with different contents were studied. Experiments show that the compounds consist of a magnetic perovskite phase and non-magnetic CeO2 and Mn3O4. The resistivity and magnetoresistance ratio （MR） of the samples vary with changing x. Their room-temperature MR reaches -3% - - 14% at the magnetic field of 1 T. For x =0; x =0.037 and x = 0.26 samples, the conductance keeps unchanged basically in a relatively wide temperature range above 600 K, and the result shows that it is feasible for producing SOFC cathode materials with these samples.
Phase structures, the transport ana magnetic properties of the Perovskite-type manganite （La0.8-x CexSr0.2）0.97 MnO3（x = 0 - 0. 26） prepared by La2O3 containing CeO2 with different contents were studied. Experiments show that the compounds consist of a magnetic perovskite phase and non-magnetic CeO2 and Mn3O4. The resistivity and magnetoresistance ratio （MR） of the samples vary with changing x. Their room-temperature MR reaches -3% - - 14% at the magnetic field of 1 T. For x =0; x =0.037 and x = 0.26 samples, the conductance keeps unchanged basically in a relatively wide temperature range above 600 K, and the result shows that it is feasible for producing SOFC cathode materials with these samples.