摘要
Poly（phenylene sulfide/ether） （PPSE） was synthesized from 4,4＇-dihydroxydiphenyl sulfide and 4,4＇-dichlorodiphenyl sulfide in solution by nucleophilic substitution reaction. The resulting polymer was characterized by viscosity measurement, elemental analysis, FT-IR, ^1H NMR, X-ray diffraction and thermal analysis. The results showed that the viscosities of the resulting polymer were above 0.68 dL/g, and the linear chain structure of product was confirmed. PPSE had the same reflex indices as poly（p-phenylene sulfide）, an orthorhombic crystalline with unit cell a=0.853, b=0.562, c=1.026nm. The melting temperature, glass transition temperature and initial decomposition temperature were found to be 228℃, 85℃ and 325℃, respectively. The product was soluble in common organic solvents such as NMP, N, N＇-dimethylformamide, N, N＇-dimethylacetamide and 1,2-dichloroethane.
Poly（phenylene sulfide/ether） （PPSE） was synthesized from 4,4＇-dihydroxydiphenyl sulfide and 4,4＇-dichlorodiphenyl sulfide in solution by nucleophilic substitution reaction. The resulting polymer was characterized by viscosity measurement, elemental analysis, FT-IR, ^1H NMR, X-ray diffraction and thermal analysis. The results showed that the viscosities of the resulting polymer were above 0.68 dL/g, and the linear chain structure of product was confirmed. PPSE had the same reflex indices as poly（p-phenylene sulfide）, an orthorhombic crystalline with unit cell a=0.853, b=0.562, c=1.026nm. The melting temperature, glass transition temperature and initial decomposition temperature were found to be 228℃, 85℃ and 325℃, respectively. The product was soluble in common organic solvents such as NMP, N, N＇-dimethylformamide, N, N＇-dimethylacetamide and 1,2-dichloroethane.