The fracture toughness (KIC) values determined by indentation microfracture method (IM ) for SiC whisker reinforced Al2O3 and ZrO2 based composites were calculated with different IM equations and compared with those obtained by singte edge notched beam (SENB) technique. Experimental results show that the KIC (IM) values calculated with different equations are quite different one from another. For composites without phase transformable components the KIC (IM) and KIC (SENB) values are practically on the same level, but for composites with phase transformable components (partially stabilized zirconia) the KIC (SENB) values are always higher than KIC (IM). This is because that the IM method can not reveal sensitively the toughening effect due to dynamic t-m transformation of ZrO2 as the SENB method does. The accuracy of the IM method depends on the Suitability of the IM equations and was evaluated for the materials used in this investigation. Two new IM equations are suggested with which the KIC (IM ) values can be obtained very close to KIC (SENB) values for composites having phase transformable components.
The fracture toughness (KIC) values determined by indentation microfracture method (IM ) for SiC whisker reinforced Al2O3 and ZrO2 based composites were calculated with different IM equations and compared with those obtained by singte edge notched beam (SENB) technique. Experimental results show that the KIC (IM) values calculated with different equations are quite different one from another. For composites without phase transformable components the KIC (IM) and KIC (SENB) values are practically on the same level, but for composites with phase transformable components (partially stabilized zirconia) the KIC (SENB) values are always higher than KIC (IM). This is because that the IM method can not reveal sensitively the toughening effect due to dynamic t-m transformation of ZrO2 as the SENB method does. The accuracy of the IM method depends on the Suitability of the IM equations and was evaluated for the materials used in this investigation. Two new IM equations are suggested with which the KIC (IM ) values can be obtained very close to KIC (SENB) values for composites having phase transformable components.