凝胶-模板法制备高比表面积氧化镁 被引量:16

Preparation of High Specific Surface Area MgO by a Gel-Templating Route
下载PDF
导出
摘要 以四水乙酸镁为前驱体,以大米粉形成的凝胶为模板,采用新的凝胶-模板法制备了一系列的氧化镁材料,并用X射线衍射、扫描电镜、低温氮气吸附-脱附、X射线荧光分析、热重-差示扫描量热、CO2程序升温脱附和氨程序升温脱附等手段对样品进行了表征.该方法主要利用大米粉在水中加热形成凝胶来分散镁盐前驱体,再通氧焙烧去除模板从而获得多孔MgO材料.结果表明,制得的MgO具有高比表面积(可达206m^2/g)和双介孔结构(孔径分别位于3.9和5~40nm附近).与直接焙烧四水乙酸镁制得的MgO相比,这类新型高比表面积MgO具有较多的强碱位和较少的酸性位,并在异丙醇催化分解反应中表现出更高的丙酮收率和选择性,有望成为一类优良的固体碱催化剂. A series of solid base MgO materials were prepared by a new gel-templating route using the gel derived from rice powder as the template and Mg(CH3COO)2·4H2O as the MgO precursor. The samples were characterized by X-ray diffraction, scanning electron microscopy, nitrogen adsorption-desorption, X-ray fluorescence, thermogravimetry-differential scanning calorimetry, and CO2 and NH3 temperature-programmed desorption. In this route, magnesium acetate was dispersed by rice gel that was formed from rice powder after heating in water, and the porous MgO material was obtained after the gel template was removed by calcination in oxygen. The as-prepared MgO material has high specific surface area (206 m^2/g) and bi-mesopore structure with pore size around 3.9 and 540 nm. Compared with the MgO prepared by direct thermal decomposition of the MgO precursor, the novel high-specific-surface-area MgO material contains more strong basic sites and less acidic sites and exhibited higher acetone yield and selectivity in isopropanol decomposition, making it a potential solid base catalyst.
出处 《催化学报》 SCIE CAS CSCD 北大核心 2009年第7期631-636,共6页
基金 国家自然科学基金(20873061) 国家高技术研究发展计划(863计划 2008AA06Z327) 南京大学开放测试基金
关键词 凝胶-模板法 氧化镁 大米粉 纳米材料 高比表面积 gel-templating route magnesia rice powder nanomaterial high specific surface area
  • 引文网络
  • 相关文献

参考文献20

  • 1Aramendia M A,Borau V,Jimenez C,Marinas J M,Ruiz J R,Urbano F J.Appl Catal A,2003,244:207.
  • 2Xu B Q,Wei J M,Wang H Y,Sun K Q,Zhu Q M.Catal Today,2001,68:217.
  • 3Klabunde K J,Stark J,Koper O,Mohs C,Park D G,Decker S,Jiang Y,Lagadic I,Zhang D J.J Phys Chem,1996,100:12142.
  • 4Ranjit K T,Klabunde K J.Chem Mater,2005,17:65.
  • 5Yu J C,Xu A W,Zhang L Zh,Song R Q,Wu L.J Phys Chem B,2004,108:64.
  • 6Martin M E,Narske R M,Klabunde K J.Microporous Mesoporous Mater,2005,83:47.
  • 7Kim J Y,Jung H S,Hong K S.J Am Ceram Soc,2005,88:784.
  • 8Cushing B L,Kolesnichenko V L,O'Connor C J.Chem Rev,2004,104:3893.
  • 9Li W C,Lu A H,Weidenthaler C,Schüth F.Chem Mater,2004,16:5676.
  • 10刘水刚,黄世勇,李军平,赵宁,魏伟,孙予罕.活性炭模板制备的多孔固体碱催化酯交换反应[J].石油化工,2007,36(12):1250-1254. 被引量:10

二级参考文献50

  • 1李向召,江琦.固体碱催化剂研究进展[J].天然气化工—C1化学与化工,2005,30(1):42-48. 被引量:34
  • 2蒋绍亮,章福祥,关乃佳.固体碱催化剂在催化反应中的应用进展[J].石油化工,2006,35(1):1-10. 被引量:30
  • 3管洪波,王培,王晖,赵璧英,朱月香,谢有畅.高比表面纳米MgO的制备及其影响因素研究[J].物理化学学报,2006,22(7):804-808. 被引量:13
  • 4管洪波,王培,赵璧英,朱月香,谢有畅.低温固相法制备高比表面积的纳米MgO[J].催化学报,2006,27(9):793-798. 被引量:20
  • 5周广栋,韩洋,刘杰,李丽敏,甄开吉,王海水,程铁欣.氧化镁负载的钼钒磷酸铜催化剂的积碳行为[J].高等学校化学学报,2007,28(2):297-301. 被引量:4
  • 6MARIA AA, VICTORIANO B, CESAR J. et al. Influence of the preparation method on the structural and surface properties of various magnesiunl oxides and their catalytic activity in the Meerwein-Ponndorf-Verley reaction [J]. Appl Catal A:General, 2003, 244:207-215.
  • 7STARK J V, KLABUNDE K J. Nanoscalc metal oxide particles, Clllsters as chemical reagents: uni(tHe surface chemistry on magnesium oxide as shown by enhanced adsorption of acid gases[J]. Chem Mater, 1996, 8(8):1904-1912.
  • 8STOIMENOV P K, KLINGER R L, MARCHING L, et aL.Metal oxidenanoparticles as bactericidalagents[J]. Langmuir,2002, 18:6679-6686.
  • 9HAN YC, LI S P, WANG X Y, et al. Synthesis and sintering of nanocrystalline hydroxyapatite powders by citric acid sol-gel combustion method [J]. Mater Res Bull, 2004, 39:25-32.
  • 10KIM H M, KIM Y, PARK S J, REY C, etal. Thin film of low crystalline calcium phosphate apatite formed at low ternperature [J]. Biomaterials, 2000, 21:1129-34.

共引文献44

同被引文献273

引证文献16

二级引证文献57

;
使用帮助 返回顶部