摘要
In order to investigate the laws of variation on tensile strength of butt welded joint post high temperatures, the wide plate tension tests for butt welded joint were conducted after cooling down from different high temperatures. The tests indicate that specimens appear ductile fracture at the steel plate during the tension tests after cooling down. The maximum temperatures undergone and the cooling pattern are major factors influencing tensile strength of butt welded joint post high temperatures. The tensile strength mostly reduces by 8% within 900℃. Based on the experimental results, the paper proposes the calculation formulas of tensile strength of butt welded joint post high temperatures. The conclusions of the paper supply references for evaluation damage and reinforcement of steel structure post fire.
In order to investigate the laws of variation on tensile strength of butt welded joint post high temperatures, the wide plate tension tests for butt welded joint were conducted after cooling down from different high temperatures. The tests indicate that specimens appear ductile fracture at the steel plate during the tension tests after cooling down. The maximum temperatures undergone and the cooling pattern are major factors influencing tensile strength of butt welded joint post high temperatures. The tensile strength mostly reduces by 8% within 900℃. Based on the experimental results, the paper proposes the calculation formulas of tensile strength of butt welded joint post high temperatures. The conclusions of the paper supply references for evaluation damage and reinforcement of steel structure post fire.