热变形参数对GH864合金显微组织的影响 被引量:4

Effects of Hot-Working Parameters on Microstructure of GH864 Superalloy
下载PDF
导出
摘要 采用等温热压缩的方法研究了在变形温度为1000~1160℃、应变速率为1和10s-1、工程应变量为30%,50%和70%时,不同的热变形参数对GH864合金流变应力和显微组织的影响。结果表明,当变形温度低于γ′相析出温度时,动态再结晶能力较差。在高于MC碳化物的回溶温度变形时,由于沿晶界再析出的细小MC颗粒对晶界的非均匀钉扎作用,容易得到混晶严重的热处理态组织。降低变形速率和增加变形量可以得到较为均匀的变形态组织,最终改善热处理态的混晶程度。GH864合金热变形温度的下限和上限分别为γ′相的析出温度和MC碳化物的回溶温度。 The effects of hot working parameters on flow stress and microstructure of GH864 superalloy were studied by isothermal compressive deformation at deformation temperatures from 1000 to 1160 ℃, strain rates of 1 and 10 s^-1 and engineering strain of 30%, 50% and 70%. The results show that the deformation temperature has great influence on the ultimate as-heat treated grain size and morphology of carbides on grain boundary. When the temperature is below the γ' precipitation temperature, the dynamic recrystallization capability is bad. While when the temperature is high enough to resolve MC carbides, severely duplex grain structure and feather-like carbide around smaller grains can be easily formed because of the non-uniform pinning effect of re-precipitated fine MC particles on grain boundary, and all these unfavorable characteristics can be partially eliminated by improving hot deformed structure through increasing strain and decreasing strain rate. The ideal deformation temperature should be confined between γ' precipitation temperature and dissolution of MC carbide.
机构地区 北京科技大学
出处 《稀有金属材料与工程》 SCIE EI CAS CSCD 北大核心 2010年第4期608-612,共5页 Rare Metal Materials and Engineering
基金 国家自然科学基金(50771011)
关键词 GH864合金 热变形参数 动态再结晶 晶界碳化物 GH864 superalloy hot-working parameters dynamic recrystallization carbides on grain boundary
  • 引文网络
  • 相关文献

参考文献12

  • 1KurtPRohrbach.宇航材料工艺,2005,(1):61-61.
  • 2Alniak M Oktay,Fevzi Bedir.Materials Science & Engineering A[J],2006,429:295.
  • 3Medeiros S C,Prasad Y V R K,Frazier W G et al.Materials Science & Engineering A[J],2000,293:198.
  • 4Salehi A R,Serajzadeh S,Yazdipour N.Materials Chemistry and Physics[J],2007,101(1):153.
  • 5张北江,赵光普,胥国华,冯涤.GH742合金热变形行为与微观组织演化[J].金属学报,2005,41(11):1207-1214. 被引量:27
  • 6Vardar N,Ekerim A.Engineering Failure Analysis[J],2007,14:743.
  • 7Holzapfel C,Schaf W,Marx M et al.Scripta Materialia[J],2007,56:697.
  • 8HongChengmiao(洪成淼) YaoZhihao(姚志浩) Zhangmaicang(张麦仓)etal.北京科技大学学报,2008,30(9):1020-1020.
  • 9Young-Sang Na,Jong-Taek Yeom,Nho-Kwang Park et al.Journal of Materials Processing Technology[J],2003,141:337.
  • 10张北江,赵光普,焦兰英,胥国华,秦鹤勇,冯涤.热加工工艺对GH4586合金微观组织的影响[J].金属学报,2005,41(4):351-356. 被引量:37

二级参考文献46

  • 1宋晓艳,R.Markus,张久兴.含有两尺寸组粒子分布的多相材料再结晶的研究[J].金属学报,2004,40(10):1009-1017. 被引量:10
  • 2赵光普.金属学报,1995,31:193-193.
  • 3Xie S S, Wang T L, Lu J Y. Mater Sci Technol, 1999;15(5): 411.
  • 4崔彤 王磊 吕俊英 杨洪才 赵光普.钢铁研究学报,2003,15(7):21-21.
  • 5Meyers M A, Benson D J, Vohringer O, Kad B K, Xue Q,Fu H H. Mater Sci Eng, 2002; A322:194.
  • 6Cheng L M, Poole W J, Embury J D, Lloyd D J. Metall Mater Trans, 2003; 34A: 2473.
  • 7Mecking H, Kocks U F. Acta Metall, 1981; 29:1865.
  • 8Martin J L, Piccolo B L, Kruml T, Bonneville J. Mater Sci Eng, 2002; 322A: 118.
  • 9Walgraef D. Mater Sci Eng, 2002; 322A: 167.
  • 10Tian B, Zickler G A, Lind C, Paris O. Acta Mater, 2003;51:4149.

共引文献59

同被引文献44

引证文献4

二级引证文献37

;
使用帮助 返回顶部