Perovskite-type oxygen-permeable membrane reactors of BaCo0.7Fe0.2Nb0.1O3-δ （BCFNO） packed with Ru-based catalyst had high oxygen permeability and could be used for hydrogen production by partial oxidation of methane in coke oven gas （COG）. At 1173 K, 94% of methane conversion, 85% of H2 selectivity, 107% of CO selectivity, and as high as 15.4 mL·cm^-2·min^-1 of oxygen permeation flux were obtained. The BCFNO membrane itself had poor catalytic activity to partial oxidation of CH4 in COG. During continuous operation for 70 h at 1173 K, no degradation of the membrane reaction performance was observed. XRD and SEM characterization also demonstrated that the BCFNO membrane reactor exhibited good stability in partial oxidation of methane in COG.
Perovskite-type oxygen-permeable membrane reactors of BaCo0.7Fe0.2Nb0.1O3-δ （BCFNO） packed with Ru-based catalyst had high oxygen permeability and could be used for hydrogen production by partial oxidation of methane in coke oven gas （COG）. At 1173 K, 94% of methane conversion, 85% of H2 selectivity, 107% of CO selectivity, and as high as 15.4 mL·cm^-2·min^-1 of oxygen permeation flux were obtained. The BCFNO membrane itself had poor catalytic activity to partial oxidation of CH4 in COG. During continuous operation for 70 h at 1173 K, no degradation of the membrane reaction performance was observed. XRD and SEM characterization also demonstrated that the BCFNO membrane reactor exhibited good stability in partial oxidation of methane in COG.
基金
supported by the National High-Tech Research and Development Program of China (No. 2006AA11A189)
the Research on Novel Technology of Hydrogen Production from Oven Gas from Metallurgy Process (No. 07DZ12036)
the National Key Technolo-gies Research and Development Program of China (No. 2006BA103A05)