摘要
The effects of ZnO-B2O3 （ZB2） on the sintering behavior and microwave dielectric properties of （Ca0.254Li0.19Sm0.14）TiO3 ceramics were investigated. The densities of the specimens reached the maximum value by adding 3 wt.% ZB2 and then decreased. The sintering temperature of the specimens was lowered from 1300 to 1100℃ without degradation of the microwave dielectric properties. The （Ca0.254Li0.19Sm0.14）TiO3＋ 3 wt.% ZB2 sintered at 1100℃ for 3 h showed good microwave dielectric properties, εr= 108.2, Qf= 6545 GHz, and rf= 6.5 ppm/℃, respectively, indicating that ZB2 was an effective sintering aid to improve the densification and microwave dielectric properties of （Ca0.254Li0.19Sm0.14）TiO3 ceramics.
The effects of ZnO-B2O3 （ZB2） on the sintering behavior and microwave dielectric properties of （Ca0.254Li0.19Sm0.14）TiO3 ceramics were investigated. The densities of the specimens reached the maximum value by adding 3 wt.% ZB2 and then decreased. The sintering temperature of the specimens was lowered from 1300 to 1100℃ without degradation of the microwave dielectric properties. The （Ca0.254Li0.19Sm0.14）TiO3＋ 3 wt.% ZB2 sintered at 1100℃ for 3 h showed good microwave dielectric properties, εr= 108.2, Qf= 6545 GHz, and rf= 6.5 ppm/℃, respectively, indicating that ZB2 was an effective sintering aid to improve the densification and microwave dielectric properties of （Ca0.254Li0.19Sm0.14）TiO3 ceramics.
基金
supported by the National Natural Science Foundation of China (No. 50572008)