Effects of deformation temperature on the mechanical properties and microstructure of lean duplex stainless steels B2102 and S32101 have been investigated. It was found that the strength decreased continuously with increases in temperature from -60 ℃ to 100 ℃. The strength of S32101 was higher than that of B2102 owing to its higher nitrogen content. Plasticity of B2102 increased with an increase in deformation temperature from - 60 ℃ and reached the optimal elongation ratio of 49% - 54% after deformation at 20 - 50 ^（2. Martensite transformation was observed during deformation due to the transformation-induced plasticity effect. The optimal elongation was achieved at deformation temperatures close to the Md（3O/50） temperatures of 62 ℃ and 6 ℃ for B2102 and S32101. respectively.
Effects of deformation temperature on the mechanical properties and microstructure of lean duplex stainless steels B2102 and S32101 have been investigated. It was found that the strength decreased continuously with increases in temperature from -60 ℃ to 100 ℃. The strength of S32101 was higher than that of B2102 owing to its higher nitrogen content. Plasticity of B2102 increased with an increase in deformation temperature from - 60 ℃ and reached the optimal elongation ratio of 49% - 54% after deformation at 20 - 50 ^（2. Martensite transformation was observed during deformation due to the transformation-induced plasticity effect. The optimal elongation was achieved at deformation temperatures close to the Md（3O/50） temperatures of 62 ℃ and 6 ℃ for B2102 and S32101. respectively.
基金
sponsored by the Project of Shanghai Industrial Application of New and HighTechnologies in 2009