Operating condition and service results of several tested bricks in slagline area of the VOD vessel are described. It has been shown that the fully co-clinkered magnesite chrome brick is superior, followed by two-stage calcined magnesite-dolomite brick , prereacted magnesite-chrome brick and one-stage calcined magnesite-dolomite brick. Chemical and petrological examination were carried out by conventional analysis and optical microscope respectively. The reason of damage of the tested bricks are discussed and described as follows : (1) MgO in brick is erased and dissolved by slag to destroy structure of the direct bond ; (2) slag penetrating into the brick and then reacting with it to form various belts leading to spatting ; (3 ) reducing action of reducing agents ; (4) vaporization of some composition in the brick at high temperature under vacuum causes reducing weight and increasing porosity and (5 ) serious ma-chanic abrasion. Therefore, some opinions on increasing lining life of VOD vessels are suggested.
Operating condition and service results of several tested bricks in slagline area of the VOD vessel are described. It has been shown that the fully co-clinkered magnesite chrome brick is superior, followed by two-stage calcined magnesite-dolomite brick , prereacted magnesite-chrome brick and one-stage calcined magnesite-dolomite brick. Chemical and petrological examination were carried out by conventional analysis and optical microscope respectively. The reason of damage of the tested bricks are discussed and described as follows : (1) MgO in brick is erased and dissolved by slag to destroy structure of the direct bond ; (2) slag penetrating into the brick and then reacting with it to form various belts leading to spatting ; (3 ) reducing action of reducing agents ; (4) vaporization of some composition in the brick at high temperature under vacuum causes reducing weight and increasing porosity and (5 ) serious ma-chanic abrasion. Therefore, some opinions on increasing lining life of VOD vessels are suggested.