Elimination of cracks in stainless steel casings via 3D printed sand molds with an internal topology structure

下载PDF
导出
摘要 The important supporting component in a gas turbine is the casing,which has the characteristics of large size,complex structure,and thin wall.In the context of existing 3DP sand casting processes,casting crack defects are prone to occur.This leads to an increase in the scrap rate of casings,causing significant resource wastage.Additionally,the presence of cracks poses a significant safety hazard after the casings are put into service.The generation of different types of crack defects in stainless steel casings is closely related to casting stress and the high-temperature concession of the sand mold.Therefore,the types and causes of cracks in stainless steel casing products,based on their structural characteristics,were systematically analyzed.Various sand molds with different internal topology designs were printed using the 3DP technology to investigate the impact of sand mold structures on high-temperature concession.The optimal sand mold structure was used to cast casings,and the crack suppression effect was verified by analyzing its eddy current testing results.The experimental results indicate that the skeleton structure has an excellent effect on suppressing cracks in the casing.This research holds important theoretical and engineering significance in improving the quality of casing castings and reducing production costs.
出处 《China Foundry》 SCIE EI CAS CSCD 2024年第4期319-326,共8页 中国铸造(英文版)
基金 financially supported by the National Natural Science Foundation of China(No.52175352) the Xing Liao Ying Cai Project of Liaoning Province(No.XLYC2008036) the Shenyang Youth Innovation Talent Support Program(No.RC220429)。
  • 相关文献

参考文献9

二级参考文献68

共引文献57

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部