摘要 通过对连续热处理过程中受到不同张力的超窄2Cr13带钢进行盐雾实验以及金相组织观察,探讨了超窄2Cr13带钢生产过程中张力对其耐腐蚀性能的影响。结果表明,当带钢所加载的张力不超过98 N(宽度减小率不超过1.8%)时,试样的耐腐蚀性能不会产生变化;当带钢所加载的张力大于98 N(宽度减小率超过1.8%)时,试样的耐腐蚀性能随着张力的增大而变差。 According to the salt mist test and observation on the microstructure of the super narrow 2 Cr13 steel strip during continuous heat treatment under different tension,the influence of the tension on the corrosion resistance of super narrow 2 Cr13 steel strip were discussed.The result shows that when the tension loaded on the steel strip no more than 98 N(the width reduce rate no more than 1.8%),the corrosion resistance of the sample does not change.When the tension loaded on the steel strip more than 98 N(the width reduce rate more than 1.8%),the corrosion resistance of the sample become weak as the tension raise.
作者 朱晨 金莹 刘小英 张娟荣 袁亚 刘雯 ZHU Chen;JIN Ying;LIU Xiao-ying;ZHANG Juan-rong;YUAN Ya;LIU Wen(Xianyang Vocational Technical College,Xianyang 712046,China)
出处 《轧钢》 2020年第1期30-32,共3页 Steel Rolling
基金 咸阳职业技术学院2019年度科学研究项目(2019KYB02).
关键词 超窄带钢 张力 耐腐蚀性能 宽度减小率 super narrow steel strip tension corrosion resistance width reduce rate
  • 相关文献

参考文献2

二级参考文献3

  • 1Carlsson B. The contact pressure distribution in flat rolling of wire[J]. J Mater Process Teehnol, 1998,73 : 1.
  • 2Carlsson B, Lagergren J. The deformation of drawn wire in flat rolling[C]//ESDA 96, Third Biennial Joint Conference on Engineering Systems, Design and Analysis. New York: ASME, 1996 : 175.
  • 3王文学,刘彩玲,王雨,杨拉道,左雁冰.2Cr13不锈钢高温特性及对连铸保护渣的要求[J].钢铁钒钛,2008,29(1):61-65. 被引量:9

共引文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部