摘要
本文以一水合乙酸铜为铜源,N,N-二甲基甲酰胺(DMF)为溶剂,聚乙烯吡咯酮(PVP)为模板剂,采用静电纺丝技术制备了Cu(CH_(3)COO)_(2)/PVP复合纳米纤维.将上述复合纳米纤维在650℃焙烧,成功制备了CuO纳米纤维.分别利用X射线衍射仪(XRD),傅里叶光谱(FT-IR)和光致发光光谱(PL)进行了表征.本文为其他金属氧化物纳米纤维的制备提供了新思路.
In this paper,Cu(CH_(3)COO)_(2)/PVP composite fiber membrane was prepared by electrospinning with copper acetate monohydrate as copper source,N,N-dimethylformamide(DMF)as solvent and polyvinylpyrrolidone(PVP)as template.CuO nanofibers were successfully prepared by calcining the composite nanofiber at 650℃.The samples were characterized by X-ray diffraction(XRD),Fourier transform spectroscopy(FT-IR)and photoluminescence(PL)in details.This paper provides new ideas for the preparation of other metal oxide nanofibers.
作者
周倍汇
毕菲
李慧
付晓雨
王立艳
赵丽
盖广清
肖姗姗
ZHOU Bei-hui;BI Fei;LI Hui;FU Xiao-yu;WANG Li-yan;ZHAO Li;GAI Guang-qing;XIAO Shan-shan(Engineering laboratory of building energy saving technology,Jilin Jianzhu university,Changchun 130118,China)
出处
《吉林建筑大学学报》
CAS
2022年第6期47-50,共4页
Journal of Jilin Jianzhu University
基金
吉林省科技厅自然科学基金项目(YDZJ202201)
吉林省科技厅优秀青年人才基金项目(20170520152JH)
吉林省科技厅自然科学基金项目(20210101401JC)
吉林省教育厅“十三五”科学技术项目(JJKH20180580KJ)
吉林省产业技术研究与开发项目(2019C059)
关键词
静电纺丝技术
纳米纤维
氧化铜
electrospinning technology
nanofibers
copper oxide