CuO-modified activated carbon for the improvement of toluene removal in air

We used an impregnation method to prepare CuO/AC(activated carbon) composite materials of different CuO content and characterized them via scanning electron microscope(SEM), Brunauer–Emmett–Teller(BET), and Fourier transform infrared spectroscopy(FT-IR).The effect of CuO content on toluene adsorption/desorption was evaluated.We explored the reusability of AC and AC03(CuO modified AC with CuO loading 0.3 wt.%) adsorbents via toluene adsorption/desorption cycle testing.We used quasi-firstand quasi-second-order models, the Bangham model, and the Weber–Morris model to fit the toluene adsorption data.The introduction of CuO species evidently improved the adsorption performance of activated carbon toward toluene.The CuO content markedly affected the specific surface area, CuO dispersal, the numbers of oxygen-containing functional groups on the surface, and adsorption performance of the prepared composite adsorbents.Low CuO content was not favorable for the formation of active adsorption sites,while high content greatly reduced the specific surface area, and even covered active adsorption sites.The toluene adsorption performance varied in the order AC03 > AC02 >AC05 > AC08 > AC01(AC03, AC02, AC05, AC08 and AC01 are CuO modifying AC with CuO loading 0.3, 0.2, 0.5 0.8 and 0.1 wt.%, respectively).The breakthrough time and toluene adsorption capacity of the AC03 composite adsorbent were 94 min and 701.8 mg/g,respectively, and the recycling efficiency was 92.8% after thermal desorption at 200°C.The adsorption process was best described by the Bangham model and adsorption could be divided into three stages.