Constructing Carbon Nanobubbles with Boron Doping as Advanced Anode for Realizing Unprecedently Ultrafast Potassium Ion Storage

Carbonaceous material with favorable K^(+)intercalation feature is considered as a compelling anode for potassium-ion batteries(PIBs).However,the inferior rate performance and cycling stability impede their large-scale application.Here,a facile template method is utilized to synthesize boron doping carbon nanobubbles(BCNBs).The incorporation of boron into the carbon structure introduces abundant defective sites and improves conductivity,facilitating both the intercalation-controlled and capacitivecontrolled capacities.Moreover,theoretical calculation proves that boron doping can effectively improve the conductivity and facilitate electrochemical reversibility in PIBs.Correspondingly,the designed BCNBs anode delivers a high specific capacity(464 mAh g^(-1)at 0.05 A g^(-1))with an extraordinary rate performance(85.7 mAh g^(-1)at 50 A g^(-1)),and retains a considerable capacity retention(95.2%relative to the 100th charge after 2000 cycles).Besides,the strategy of pre-forming stable artificial inorganic solid electrolyte interface effectively realizes high initial coulombic efficiency of 79.0%for BCNBs.Impressively,a dual-carbon potassium-ion capacitor coupling BCNBs anode displays a high energy density(177.8 Wh kg^(-1)).This work not only shows great potential for utilizing heteroatom-doping strategy to boost the potassium ion storage but also paves the way for designing high-energy/power storage devices.