摘要
本文研究了模壁润滑温压部分扩散预合金Fe-2Cu-2Ni-1Mo-1C材料的烧结硬化性能,讨论了冷却速度对材料力学性能和显微组织的影响。部分扩散预合金Fe-2Cu-2Ni-1Mo-1C粉末采用模壁润滑温压压制,1 150℃氢气氛保护下烧结60 min,在900℃~600℃温度冷却区间以4.6℃/s,2.9℃/s,1.5℃/s三种速度快速冷却。试验结果显示:材料的抗拉强度和表观硬度随冷却速度的增大而升高,延伸率却随冷却速度增大而降低。在4.6℃/s的冷却速度下,Fe-2Cu-2Ni-1Mo-1C材料的抗拉强度为872 MPa,表观硬度为257 HB,明显高于2.9℃/s和1.5℃/s冷却条件下的性能。烧结硬化后材料尺寸有轻微收缩,但呈现出良好的尺寸稳定性。材料的烧结密度稍有降低。烧结硬化材料的显微组织为马氏体、贝氏体、珠光体和富镍残余奥氏体共存。马氏体含量随冷却速度增大而增加,低速冷却下组织主要为珠光体、残余奥氏体。
Sinter-hardening properties of compacts formed by partiall-diffusion alloyed Fe-2Cu-2Ni-1Mo-1C powders were investigated.Samples were formed by warm compaction with wall lubricated die,then sintered in hydrogen atmosphere at 1 150℃ for an hour and cooled at three different rates,4.6℃/s,2.9℃/s,1.5℃/s,respectively,from 900℃ to 600℃.Effect of cooling rate on mechanical properties and microstructure of the materials is discussed.Results show that when cooling rate increases,mechanical properties of the material...
出处
《粉末冶金工业》
CAS
北大核心
2007年第6期9-13,共5页
Powder Metallurgy Industry
基金
国家和广东省自然科学基金项目(50574041
06105411)
广东省及广州市科技项目(2004B10301018
20021-D6081)
教育部新世纪优秀人才项目(NCET-05-0739)
关键词
模壁润滑温压
烧结硬化
力学性能
显微组织
warm compaction with wall lubricated die
sinter-hardening
mechanical property
microstructure